analysis pengaruh kedalaman alur back chipping terhadap serangan stress corrosion cracking pada material SA 283 Grade C

analysis of the influence of groove depth back chipping against stress corrosion cracking in materials SA 283 Grade C

Fandy Rachmat Priambodo (6710040022)


Abstrak

Dalam dunia industri , proyek pembangunan selalu berhubungan dengan konstruksi terutama konstruksi baja. Banyak sekali macam dari konstruksi baja dan salah satunya adalah tangki penyimpanan (storage tank). Setiap pembuatan tangki penyimpanan selalu ingin tangki tersebut dapat beroperasi sesuai dengan yang diharapkan. Korosi merupakan salah satu penyebab tangki tersebut tidak dapat memenuhi waktu operasi yang diinginkan. Banyak sekali macam-macam dari korosi tapi dalam tugas akhir ini yang difokuskan adalah korosi SCC. SCC (Stress Corrosion Cracking) merupakan suatu bentuk korosi yang tersembunyi, yang ditandai hilangnya kekuatan mekanis dan dapat memicu retak cepat serta kegagalan struktur.SCC hanya akan terjadi apabila efek gabungan tiga faktor secara bersamaan yaitu lingkungan yang agresif, material yang sensitif dan tegangan tarik yang tinggi, tegangan ini dapat muncul dari beberapa sumber yaitu: tegangan aplikasi, tegangan sisa dan tegangan thermal. Pengujian yang dilakukan terdapat 3 pengujian yaitu : Pengujian Bending, pengujian korosi SCC, pengujian penetrant. Pengujian dilakukan untuk melihat apakah material baja karbon SA 283 Grade C tahan terhadap serangan korosi SCC dengan larutan korosifnya asam sulfat. Variasi yang digunakan adalah variasi kedalaman alur back chipping 1.5, 2.5, 3.5 dan tanpa back chipping. Dari hasil pengujian maka didapatkan dari variasi diatas yang mengalami retak selama proses pengujian korosi adalah variasi dengan kedalaman back chipping 3.5 pada bagian root bend dengan panjang retak sepanjang 4.5 mm dan variasi kedalaman back chipping 2.5 pada bagian face bend.


Abstract

In the industrialized world, is always have relationship with development projects, especially construction steel construction. There are so many kinds of steel construction and one of them is the storage tank. Each manufacture of storage tanks always want the tank to operate as expected. Corrosion is one of the causes of the tank cant meet the desired operating time. There are so many kinds of corrosion but in this thesis is focused corrosion SCC. SCC (Stress Corrosion Cracking) is a form of hidden corrosion, which marked the loss of mechanical strength and can lead to cracking and failure of the structure quickly. SCC will only occur if the combined effect of three factors simultaneously is an aggressive environment, sensitive materials and high tensile stress, this stress can arise from several sources, likestress of application, residual stress and thermal stress. There are any 3 examination in this thesis is bending testing, corrosion testing and penetrant testing.The test performed to see if material carbon steel SA 283 Grade C resistant to SCC corrosive attack by corrosive sulfuric acid solution. Variation used is a variation back chipping depth of groove : 1.5, 2.5, 3.5 and without back chipping. From the test results are obtained from the above variations are experiencing cracking during the process of corrosion testing is a variation without back chipping withcrack a length of 4.5 mm and variation back chipping 2.5 with crack a length 4.5mm.


Detil Peneliti

Dosen Pembimbing 1 :Wiwik Dwi Pratiwi
Dosen Pembimbing 2 :

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.