PENGARUH MULTIPLE REPAIR DISSIMILAR MATERIAL AUSTENITIC STAINLESS STEEL DENGAN MILD STEEL TERHADAP NILAI KEKERASAN, STRUKTUR MIKRO, DAN LAJU KOROSI GALVANIK

EFFECT OF MULTIPLE REPAIR DISSIMILAR MATERIAL AUSTENITIC STAINLESS STEEL WITH MILD STEEL TO HARDNESS VALUE, MICRO STRUCTURE AND GALVANIC CORROSION RATE

Mahfud Syafiudin (6710040019)


Abstrak

ABSTRAK PENGARUH MULTIPLE REPAIR DISSIMILAR MATERIAL AUSTENITIC STAINLESS STEEL DENGAN MILD STEEL TERHADAP NILAI KEKERASAN, STRUKTUR MIKRO, DAN LAJU KOROSI GALVANIK Oleh Mahfud Syafiudin NRP : 6710040019 Kemungkinan terjadi kesalahan dalam proses pengelasan tidak dapat dihindari dan berakibat fatal. Hal ini terjadi akibat human error atau kesalahan prosedur. Untuk mengatasinya diperlukan perlakuan repair, apabila kesalahan dalam proses pengelasan dilakukan berulang kali maka perlu dilakukan multiple repair welding pada sambungan las tersebut. Akibat dari multiple repair welding yang dilakukan akan berpengaruh besar terhadap sifat mekanik, struktur mikro dan serangan korosi galvanic. Pada penelitian ini menggunakan material dissimilar joint antara mild steel A36 dengan stainless steel 316L. Penelitian ini dilakukan menggunakan proses pengelasan SMAW posisi 1G dengan variabel penelitian proses tanpa repair, repair 2X, repair 3X dan repair 4X. Sedangkan pengujian yang dilakukan ialah metallography, hardness dan korosi, agar dapat diketahui hubungan antara struktur mikro, nilai kekerasan dan ketahanan korosinya. Dari hasil pengujian didapatkan hasil uji metallography pada HAZ carbon steel mengalami penambahan karbon seiring dengan proses repair yang diberikan, terkecuali pada spesimen dengan variabel 2X repair yang tidak mengalami penambahan karbon, sedangkan pada HAZ stainless steel mengalami penambahan karbida krom seiring dengan proses repair yang diberikan, terkecuali pada variabel 2X repair yang tidak mengalami penambahan karbida krom. Pada weld metal mengalami penambahan austenite untuk variabel tanpa repair, 2X repair dan 4X repair sedangkan pada variabel 3X repair tidak terjadi penambahan unsure austenite. Dengan berubahnya struktur mikro maka sifat mekanik kekerasan mengalami kenaikan seiring dengan bertambahnya proses repair yang diberikan. Sedangkan ketahanan korosi rata-rata paling rendah terjadi pada spesimen tanpa repair dengan laju korosi sebesar 1.06452 mm/year, di ikuti dengan variabel 3X repair dengan laju korosi sebesar 0.660113 mm/year lalu di ikuti variabel 4X repair dengan laju korosi sebesar 0.433423 mm/year, dan ketahanan korosi terbaik terjadi pada variabel 2X repair dengan laju korosi sebesar 0.23179 mm/year. Kata-kata kunci : Multiple repair, hardness, micro structure, laju korosi galvanik ?


Abstract

ABSTRACT EFFECT OF MULTIPLE REPAIR DISSIMILAR MATERIAL AUSTENITIC STAINLESS STEEL WITH MILD STEEL TE TO HARDNESS VALUE, MICRO STRUCTURE AND GALVANIC CORROSION RATE Composed by: Mahfud Syafiudin NRP : 6710040019 The possibility of error in the welding process is unavoidable and fatal. This can occur due to human error or Mistake procedure. To handle the necessary treatment to repair, if the errors in the welding process is repeated multiple times it is necessary to repair welding at the weld joint. As a result of multiple repair welding is done will greatly affect the mechanical properties and micro structure especially on galvanic corrosion attack. This research was conducted using the welding process SMAW 1G position with the research process variables without repair, repair 2X, 3X repair and repair 4X. While the tests performed is metallography, hardness and corrosion, in order to know the relationship between the microstructure, hardness and corrosion resistance. From the test results obtained on the test results metallography carbon steel HAZ has the addition of carbon along with the repair process is given, except in specimens with variable 2X repair that does not undergo the addition of carbon, while the stainless steel HAZ has the addition of chromium carbide along with the repair process is given, An exception is a variable 2X repair is not increased chromium carbide. In austenitic weld metal has the addition of a variable without repair, 2X and 4X repair repair repair while the 3X variable no additional elements of austenite. By changing the structure of the micro-mechanical properties of hardness increased with increasing repair process is given. While the corrosion resistance of the average lowest occurred in specimens without repair the corrosion rate of 1.06452 mm/year, followed by a variable 3X repair the corrosion rate of 0.660113 mm/year and at follow 4X variable repair the corrosion rate of 0.433423 mm/year , and the best corrosion resistance occurs in variable 2X repair the corrosion rate of 0.23179 mm / year. Key words: Multiple repair, hardness, micro structure, the corrosion rate


Detil Peneliti

Dosen Pembimbing 1 :Muhamad Ari
Dosen Pembimbing 2 : Zuhri Noor

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.