PENGARUH PENGELASAN GANDA / DOUBLE SIDE WELDING TERHADAP MECHANICAL PROPERTIES DAN STRUKTUR MIKRO PADA MATERIAL SA-516 GRADE 70

THE EFFECT OF DOUBLE SIDE WELDING TO THE MECHANICAL PROPERTIES AND MICRO STRUCTURE OF MATERIAL SA-516 GRADE 70

Timur Aditya Pambudi (6710040014)


Abstrak

Teknologi dalam pengelasan sangat berkembang dengan pesat dimana untuk memperbaiki hasil pengelasan yaitu dilakukan proses double side welding, yang juga bertujuan untuk mengurangi nilai perubahan bentuk / Distorsi akibat dari proses pengelasan. Proses double side welding sangat membantu dalam menanggapi efisiensi waktu. Tetapi proses pengelasan double side welding menghasilkan panas yang lebih tinggi dan cooling rate yang lebih cepat di bandingkan proses pengelasan single side welding. Dalam dunia industri jika barang yang akan di produksi urgent maka teknik pengelasan ini sering di gunakan, Biasanya dalam pembuatanya menggunakan material SA 516 grade 70 yang memang diperuntukan untuk bejana tekan dan harus mempunyai nilai keamanan yang tinggi. Dari penelitian ini akan membandingkan bagaimana hasil nilai dari pengujian hardness test dan impact test terhadap teknik double side welding dibandingkan hasilnya dengan pengelasan yang menggunakan single side welding masing-masing dilakukan proses preheat 0?C (tanpa preheat), 100?C,dan 150?C. Dari hasil penelitian yang didapatkan semakin tinggi temperature preheat maka kekerasan akan semakin menurun dan nilai ketangguhan meningkat, nilai kekerasan paling rendah terdapat pada daerah base metal pengelasan single side welding preheat 150?C sebesar 147,6 HV, dan nilai kekerasan paling tinggi terdapat pada daerah weld metal pengelasan double side welding preheat 0?C sebesar 204 HV. Sedangkan nilai impact paling tinggi sebesar 149,5 joule terdapat di daerah takikan base metal yang dikenakan preheat 150?C pada pengelasan single side welding, dan nilai impact paling rendah sebesar 13 joule terdapat di daerah takikan base metal yang dikenakan preheat 0?C (tanpa preheat) pada pengelasan double side welding. Kata-kata kunci : preheat, double side welding, single side welding, hardness test, impact test dan struktur mikro.


Abstract

In welding technology is growing by leaps and bounds in which to improve the results of the welding done double side welding process, which also aims to reduce the value of deformation / distortion as a result of the welding process. Double side welding process is very helpful in responding to time efficiency. But the double side welding process of welding produces higher heat and faster cooling rate compared single side welding process of welding. In the industrial world if the items to be in the urgent production welding technique is often used, usually in making using material SA 516 grade 70 which is intended for pressure vessel and must have high safety value. From this study will compare how the results of testing the value of hardness test and impact test against a double side welding compared results with the use of single side welding welding masing were conducted preheat process 0?C (no preheat), 100?C, and 150?C. From the research results obtained preheat then the higher the temperature the more violent decreases and toughness value increases, the lowest hardness values found in the base metal on single side welding preheat 150?C at 147.6 HV, and the highest hardness values found in the weld metal in double side welding preheat 0?C (of 204 HV. While most high impact value for 149,5 joule contained in the base of the notch is subjected metal imposes welding preheat 150?C on single side welding, and the value of the lowest impact of 13 joule contained in the base of the notch is subjected to preheat metal wich 0? C(no preheat) in double side welding. Key words: preheat, double side welding, single side welding, hardness test, impact test and microstructure.


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : Zuhri Noor

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.