ANALISIS PENGARUH VARIASI PREHEAT PADA MATERIAL API 2H Gr 50N TO API 2W Gr 5oT TERHADAP SIFAT MEKANIK DAN KETANGGUHAN

THE EFFECT OF PREHEAT ANALYSIS ON THE MATERIAL API 2H Gr 50 N JOINT TO API 2W Gr 50 T FOR MECHANICAL PROPERTIES AND TOUGHNESS

Moch. Hilmi Akbar (6710040003)


Abstrak

ABSTRAK ANALISIS PENGARUH VARIASI PREHEAT PADA MATERIAL API 2H Gr 50 N TO API 2W Gr 50 T TERHADAP SIFAT MEKANIK DAN KETANGGUHAN Oleh : M. HILMI AKBAR NRP : 6710040003 PT. Bakrie Construction selaku fabrikator bangunan baja dan modular yang bertempat di Cilegon saat ini membangun proyek banyu urip yaitu ?Mooring Tower Project? jacket bangunan Offshore atas Client Exxon Mobil. Sesuai dengan WPS yang telah dibuat dan disepakati, bahwa proses pembangunan dan pengelasannya menggunakan Preheat sesuai dengan material yang digunakan yaitu API 2H Gr 50N to API 2W Gr 50T. Menurut teori ?Pengetahuan bahan? Preheat diperlukan agar menghasilkan sifat mekanis yang lebih baik. Dalam penelitian ini dilakukan 4 variabel, antara lain Non-Preheat, Preheat 100?C, Preheat 150?C, dan Preheat 200?C, pemanasan menggunakan brander. Material yang digunakan sesuai dengan WPS BC-STR-207 dengan proses SMAW 1G dan polarity DC ( ). Penelitian ini dilakukan dengan membandingkan hasil melalui pengujian diantaranya Tensile test, Hardness Test, Impact test. Hasil pengelasan dan pengujian specimen keempat variabel tersebut menghasilkan korelasi antara kekerasan dan kekuatan tarik material tersebut dimana hasil yang paling baik terjadi pada specimen dengan Preheat 150?C, dan untuk specimen yang mempunyai nilai ketangguhan rata-rata tertinggi terjadi pada specimen dengan preheat 100?C. Dan untuk hasil yang paling tidak baik terjadi pada specimen Non-Preheat untuk semua jenis pengujiannya. Kata kunci : Preheat, SMAW 1G, Sifat mekanis, ketangguhan.


Abstract

ABSTRACK THE EFFECT OF PREHEAT ANALYSIS ON THE MATERIAL API 2H Gr 50 N JOINT TO API 2W Gr 50 T FOR MECHANICAL PROPERTIES AND TOUGHNESS Written By : M. HILMI AKBAR NRP : 6710040003 PT. Bakrie Construction as a steel fabricator and modular buildings are located in Cilegon current project build banyu urip ie "Mooring Tower Project" Offshore construction jacket over Exxon Mobil Client. In accordance with the WPS that has been made and agreed, that the process of development and use Preheat welding according to the material used is API 2H API 2W Gr Gr 50N to 50T. According to the theory of "Knowledge of materials" Preheat is required in order to produce better mechanical properties. In this research, 4 variables, including the Non-Preheat, Preheat 100 ? C, 150 ? C Preheat, and Preheat 200 ? C, using a heating brander. The material used in accordance with the WPS BC-STR-207 with 1G SMAW process and polarity DC ( ). This research was carried out by comparing the results of such testing through Tensile test, Hardness Test, Impact Test. Results welding and testing of specimens four variables resulted in a correlation between hardness and tensile strength of the material in which the best results occurred in specimens with Preheat 150 ? C, and for specimens that have value toughness highest average occurred in specimens with a preheat of 100 ? C . And for at worst outcome occurred in specimen Non-Preheat to all types of testing. Key words : Preheat, SMAW 1G, Mechanical properties, toughness.


Detil Peneliti

Dosen Pembimbing 1 :Usman Dinata
Dosen Pembimbing 2 :

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.