ANALISIS PENGARUH EXPAND DAN SEAL WELD TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIS PADA MATERIAL TITANIUM SB 338 GRADE 2 DENGAN SA 516 GRADE 70 CLADD SB 265 GRADE 1

ANALYSIS EFFECT OF EXPAND AND SEAL WELD TO MICRO STRUKTURE AND MECHANICAL PROPERTIES FOR MATERIAL TITANIUM SB 338 GRADE 2 WITH SA 516 GRADE 70 CLADD SB265 GRADE 1

Yanuar Iskak (6709040028)


Abstrak

Perkembangan ilmu tentang material dan pengelasan sudah sangat cepat berkembang, khususnya pada material Titanium yang membutuhkan perlakuan khusus, selain itu juga faktor ekonomi yang harus diperhatikan dalam penggunaannya. Dengan menitik beratkan pada perubahan struktur mikro dan uji mekanis yang terjadi apabila dilakukan metode penyambungan pada material tersebut dengan tujuan agar dapat mengetahui seberapa besar hasil kekuatan material tersebut setelah dilakukan repair. Proses repair pada material dilakukan dikarenakan mengalami kesalahan dalam pekerjaan dilapangan ataupun saat membuat desain awal suatu produk. Dari proses repair tersebut mengakibatkan plate (material) mengalami perubahan pada struktur mikro. Untuk dapat mengetahui seberapa besar pengaruh dan perubahan pada material tersebut maka dibutuhkan suatu uji mikro test dan uji kekerasan atau hardness test. Pada hasil struktur mikro pada proses expand dan seal weld tidak banyak mengalami perubahan, dikarenakan material pada proses expand tidak mengalami perlakuan panas, sedangkan pada proses seal weld tidak mengalami perubahan yang signifikan. Untuk hasil uji makro didapatkan semua spesimen mengalami fusi yang sempurna. Hasil nilai hardness pada proses expand dan seal weld didapatkan nilai kekerasan tertinggi terletak pada proses seal weld yaitu pada bagian tubesebesar 153.77 HVN. Hal ini dikarenakan material pada tube SB 265 Grade 1 merupakan tipe material yang memang didesain untuk dapat menerima pressure yang tinggi. Kata kunci: Titanium,repair, uji mekanis, struktur mikro, SB 265 Grade 1.


Abstract

The development of the science of materials and the welding is very fast growing, especially in the Titanium material that requires special treatment, but it is also the economic factors that must be considered to use. By focusing on changes in the microstructure and mechanical test that occur when the material is done on the connection method in order to determine how much the material strength results after repair. Repair process in the material do the job due to an error in the field or when creating the initial design of a product. From the repair process resulted plate (material) changes in the microstructure. To be able to determine how much influence and change in the material it takes a micro test and hardness test. On the results of the microstructure expand and seal weld process has not changed much, because the expand material does not using heat treatment, while the seal weld process does not change significantly. Test results obtained for all specimens experienced macro perfect fusion. Results on the hardness values expand and seal weld process obtained the highest hardness value lies in the process of the seal weld on the tube is 153.77 HVN. This is because the material in tubes SB 265 Grade 1 is a type of material that is designed to accept high pressure. Keywords: Titanium, repair, mechanical test, micro structure, SB 265 Grade 1


Detil Peneliti

Dosen Pembimbing 1 :Gathot Dwi Winarto
Dosen Pembimbing 2 : Tri Karyono

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2009


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.