STUDI PENGARUH LAMA OKSIDASI DAN VARIASI METODE PEMBERSIHAN PERMUKAAN SEBELUM PENGELASAN PADA ALUMINIUM 5083 H116 DENGAN GMAW TERHADAP HASIL KUALITAS PENGELASAN

STUDY ON THE EFFECT OF TIME OXIDATION AND VARIATION METHOD ON SURFACE CLEANING BEFORE WELDING PROCESS ON ALUMINIUM 5083 H116 USING GMAW TO THE WELDING QUALITY RESULT

Imam Derajat Santoso Setiawan (6709040026)


Abstrak

STUDI PENGARUH LAMA OKSIDASI DAN VARIASI METODE PEMBERSIHAN PERMUKAAN SEBELUM PENGELASAN PADA ALUMINIUM 5083 H116 DENGAN GMAW TERHADAP HASIL KUALITAS PENGELASAN Nama Mahasiswa : 1. Imam Derajat Santoso Setiawan NRP. 6709 040 026 Nama Dosen Pembimbing : 1. Ir. Soeweify, M.Eng. 2. Ir. Muhammad Mahfud, M.MT. NIP. 195709141988031001 ABSTRAK Aluminium 5083 H116 merupakan material paduan unsur Al (aluminium) dan unsur magnesium (Mg) yang pembuatannya dengan cara strain hardening sehingga menciptakan material aluminium yang anti korosi serta memiliki kekuatan yang baik. Pengelasan aluminium memiliki permasalahan antara lain yaitu lapisan pasifnya (Al2O3) dimana apabila senyawa ini bereaksi dengan uap air akan menjadi Hydrated alumina saat aluminium terpapar dalam udara bebas pada waktu tertentu dan akan menimbulkan porosity apabila dilakukan pengelasan. Dalam kasus ini, dicari metode yang tepat supaya hasil kualitas pengelasan yang baik pada material Aluminium 5083 H116 ini. Dilakukan sebuah penelitian, dengan membiarkan material aluminium 5083 di ruangan terbuka (atmosfir) dengan metode variasi 3 pembersihan dan variasi 3 waktu lama oksidasi. Variasi pembersihan antara lain menggunakan alkohol 95%, penggerindaan, penggerindaan dan larutan kimia NaOH 10% dengan dipanaskan sampai temperatur 720C selama 45 detik kemudian dibasuh dengan air Nitrat Absolut 15% selama 2 menit kemudian dicuci dengan air dingin dan air panas lalu dikeringkan, kemudian dengan variasi waktu nol, 3 hari, dan 7 hari. Hasilnya adalah penggunaan pembersihan yang paling baik yaitu menggunakan penggerindaan larutan kimia NaOH 10% (72OC) NaNO3 15% dengan hasil porositas yang sedikit tapi memiliki kekerasan yang rendah seiiring jeda waktu yang semakin lama yaitu 71,417HVN, 69,413HVN, 68,292HVN. Dan pembersihan menggunakan alkohol 95% tidak direkomendasikan karena hasil porositas yang ditimbulkan semakin banyak seiring jeda waktu yang semakin lama. Dan untuk penggunaan pembersihan terakhir adalah penggerindaan, dari hasil porositas memang masih ada sedikit, tetapi harga kekerasannya stabil seiiring jeda waktu yang semakin lama yaitu 71,417HVN, 73,271HVN, 73,103HVN. Kata kunci : Aluminium 5083 H116, Al203, Variasi 3 pembersihan dan Variasi 3 waktu Lama Oksidasi.


Abstract

STUDY OF EFFECT OXIDATION TIME AND CLEANING VARIATION METHOD BEFORE WELDING PROCESSES ON ALUMINUM 5083 H116 WITH GMAW PROCESS REVIEWED IN WELDING QUALITY RESULT Name : 1. Imam Derajat Santoso Setiawan NRP. 6709 040 026 Advisers : 1. Ir. Soeweify, M.Eng. 2. Ir. Muhammad Mahfud, M.MT. NIP. 195709141988031001 ABSTRACT Aluminum 5083 H116 is a material alloy with alloy element of Al (aluminum) and magnesium (Mg), which are made by way of strain hardening, creating an anti-corrosion aluminum material and has good strength. Welding aluminum has problems such as the passive layer (Al2O3) which if these compounds reacting with water vapor will be hydrated alumina when the aluminum exposure in free air at a certain time and will cause porosity at applicable to welding. In this case, there is an effort to looking for the right method so that the results are good in quality of welding on Aluminum 5083 H116. Conducted to study, by letting the aluminum 5083 H116 on the open space (atmosphere) with 3 variations of the cleaning method and 3 variations of oxidation lag time. Variations among other cleanup using 95% alcohol, grinding, grinding and chemical solutions with NaOH 10% was heated to a temperature of 720C for 45 seconds and then washed with water NaNO3 15% in 2 minutes and then washed with cold water and hot water and dry them, with variation zero time, 3 days, and 7 days. The result is the best applicable of cleaning method is use a chemical solution of grinding NaOH 10% (72oC) NaNO3 15% with the result of very little porosity but have low hardness at the longer of oxidation time, the value is 71.417 HVN, 69.413HVN, 68.292 HVN. And cleaning using 95% alcohol is not recommended because the results cases of more porosity at the longer lag time. And the last is for the use of grinding, the results of the porosity is a little still there, but have a stable hardness value at the longer lag time, the value is 71.417HVN , 73.271HVN,73.103HVN. Keywords: Aluminum 5083 H116, Al203, 3 variations of cleaning method and 3 variation of oxidation lag time.


Detil Peneliti

Dosen Pembimbing 1 :Soeweify
Dosen Pembimbing 2 : Muhammad Mahfud

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2009


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.