ANALISA PENGARUH MULTIPLE REPAIR WELDING SERTA TEMPERATUR PWHT UNTUK MEMPERBAIKI MECHANICAL PROPERTIES MATERIAL PIPA SA335 GRADE 22

ANALYSIS OF MULTIPLE REPAIR WELDING EFFECT AND PWHT TEMPERATURE TO IMPROVE MECHANICAL PROPERTIES PIPE MATERIAL SA335 GRADE 22

Ricki Novianto (6709040023)


Abstrak

ABSTRAK ANALISA PENGARUH MULTIPLE REPAIR WELDING SERTA TEMPERATUR PWHT UNTUK MEMPERBAIKI MECHANICAL PROPERTIES MATERIAL PIPA SA335 GRADE 22 Oleh Ricki Novianto NRP : 6709040023 Dalam proses pembuatan super heater pada PT. ALSTOM POWER ESI di Surabaya penggunaan installasi pipa hampir digunakan pada seluruh proses produksi, Material pipa SA 335 Grade 22 merupakan salah satu jenis ferritic low alloy steel pipe for high temperatur service yang dignakan. Dalam proses pegelasan, kemungkinan terjadinya kesalahan sangatlah besar dan dapat berakibat fatal bagi struktural super heater. Kesalahan proses pengelasan dapat terjadi karena banyaknya sambungan pipa yang sulit dijangkau oleh welder serta proses heat treatment material yang akan menimbulkan kemungkinan terjadinya defect. Untuk mengatasinya defect yang terjadi maka diperlukan perlakuan repair, apabila kesalahan dalam proses pengelasan dilakukan berulang kali maka perlu dilakukan multiple repair pada weld joint tersebut. Akibat dari proses multiple repair tersebut akan berpengaruh terhadap kekerasan (hardness) material terutama pada daerah HAZ dan weld metal. Pengelasan ini dilakukan pada pipa SA335 grade 22 mengguakan metode GTAW posisi 1G (datar) dengan elektroda ER 90S-B3. Pengamatan dilakukan secara metalografis pada pengelasan sesuai WPS (tanpa Repair), repair 1x, repair 2x, repair 3x dan repair 3x serta mendapatkan heat treatment (PWHT). Repair dilakukan hingga kedalaman 40-50% weld metal. Hasil penelitian ini menunjukkan bahwa hasil repair dapat meningkatkan nilai kekerasan secara signifikan pada material non repair rata-rata HAZ sebesar 233.96 HV menjadi 289,44 HV pada material 1x repair, 279,05 pada material 2x repair, dan 279,62 HV pada material 3x repair. Penurunan kekerasan terjadi pada material 3x repair PWHT yaitu sebesar 240,59 HV. Dari hasil keseluruhan proses repair masih berada pada range kualifikasi kekerasan yaitu max.320 HV sehingga dari hasil tersebut, cut off atau pemotongan tidak perlu dilakukan. Kata Kunci : Pipe SA335 grade 22, Pengelasan GTAW, defect, multiple repair, mechanical properties


Abstract

ABSTRACT ANALYSIS OF MULTIPLE REPAIR WELDING EFFECT AND PWHT TEMPERATURE TO IMPROVE MECHANICAL PROPERTIES PIPE MATERIAL SA335 GRADE 22 By Ricki Novianto NRP : 6709040023 . In the process of making super heater at PT. ALSTOM POWER ESI in Surabaya, installation of pipes used in almost the entire production process, Material pipe SA 335 Grade 22 is one kind of ferritic low alloy steel pipe for high temperature service that is used. In the welding process, the possibility of errors is possible and would be fatal to the structural super heater. Welding process errors can happen because of many connections that are difficult to reached by pipeline welder and heat treatment process that will lead to the possibility of the occurrence of defects. To overcome this defect happens then needed treatment repair, if the errors in the welding process repeated multiple times, it is necessary to repair the weld joint. As a result of multiple repair processed will affect the hardness of material especially in the HAZ and weld metal. Welding was conducted on pipe SA335 grade 22 using GTAW method 1G position (flat) with ER 90S-B3 filler metal. Observations carried metalografis the appropriate welding WPS (without Repair), 1x repair, repair 2x, repair 3x and 3x repair and get heat treatment (PWHT). Repair carried out to a depth of 40-50% of the weld metal. These results indicate that the effect of repair can significantly increase the value of hardness on material non repair of average HAZ 233.96 HV into 289.44 HV for the 1x repair material, 279.05 HV on 2x repair materials, and 279.62 HV on 3x repair material. The decline of hardness occurred at 3x repair material PWHT that is equal to 240.59 HV. The results of overall repair process are still in the range that is max.320 HV hardness qualification, so that from these results cut off or cutting is not necessary Keywords: Pipe SA335 grade 22, GTAW Welding, defects, multiple repair, mechanical properties


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : Usman Dinata

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2009


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.