ANALISIS PERBANDINGAN PENGGUNAAN BUTTERING DAN NON BUTTERING TERHADAP PENGELASAN MATERIAL SA 283 Gr.C DENGAN SA 240 TP 904L DITINJAU DARI SIFAT MEKANIK, STRUKTUR MIKRO, DAN LAJU KOROSI

COMPARATIVE ANALYSIS USING BUTTERING AND NON-BUTTERING OF WELDING MATERIAL SA-283 GR C AND SA-240 TP 904L OBSERVED FROM MECHANICAL PROPERTIES, MICROSTRUCTURE AND CORROSION RATE

Mohamad Laist Nasser (6709040016)


Abstrak

Pengelasan dissimilar merupakan pengelasan yang dilakukan pada dua material yang berbeda. Pada penelitian ini digunakan pengelasan antara carbon steel SA-283 Gr. C dengan stainless steel SA 240 TP 904L. Pengelasan dissimilar ini diaplikasikan pada shell tangki mix acid. Pada pengelasan dissimilar material sering digunakan metode buttering, akan tetapi metode ini akan memerlukan biaya yang lebih mahal dan waktu produksi yang lebih lama. Penelitian ini akan melakukan perbandingan antara pengelasan dengan metode buttering dan tanpa menggunakan buttering, disertai dengan pembuatan WPS (welding procedure specification). Dalam penelitian ini akan dilakukan pengujian terhadap sifat mekanik yaitu tensile test dan bending test, struktur mikro, dan laju korosi nya. Pengujian tensile dan bending dilakukan sesuai dengan ASME IX, sedangkan uji korosi dilakukan dengan metode elektrokimia (sel tiga elektroda) sesuai ASTM G 102 dengan larutan uji berupa asam sulfat (H2SO4) 1M. Uji struktur mikro dilakukan dengan mikroskop optic dengan pembesaran 200X dan 500X. Hasil uji mekanik yang meliputi pengujian tarik dan bending dinyatakan accepted berdasarkan ASME IX. Uji korosi menghasilkan perbedaan laju korosi antara pengelasan dengan buttering dan non buttering. Pengelasan dengan buttering mempunyai nilai laju korosi sebesar 2.0813 ( mm/year ), sedangkan metode non buttering mempunyai laju korosi sebesar 4.0127 ( mm/year ) sehingga metode buttering mempunyai ketahanan korosi yang lebih baik daripada metode non buttering. Hasil pengujian metalografi berupa foto struktur mikro antara kedua metode tersebut tidak terdapat perbedaan. Kata Kunci : dissimilar material, uji mekanik, uji metalografi, uji korosi, WPS


Abstract

The dissimilar materials of welding are the welding on two different materials, this research using the welding between SA-283 Gr. C of carbon steel and SA 240 TP 904L of stainless steel. This dissimilar welding is applied on shell of the mix acid tank. On the dissimilar materials of welding often use buttering method, but this method need a higher cost and a longer production time. This research will be a comparison between welding buttering method without using buttering, and making its WPS (welding procedure specification). In this research will be testing the mechanical properties of the tensile test, bending test, microstructure, and its corrosion rate. Tensile test and bending test based on ASME IX, whereas testing the corrosion using three electrode cell based on ASTM G 102 with liquid of the test is sulfuric acid (H2SO4)1M. The testing of microstructure performed with an optical microscope with magnification 200 times and 500 times. After testing above, for mechanical testing which is included tensile test and bending test stated accepted base on ASME section IX. The corrosion test result difference corrosion rate between welding buttering method without using buttering, buttering method acquired corrosion rate value is 2.0813 ( mm/year ), whereas non ? buttering method has corrosion rate value is 4.0127 ( mm/year ) so that buttering method has corrosion endurance better than non ? buttering method. The result of metallography test with microstructure photo between the both of methods there is no difference. Keywords: dissimilar materials, mechanical testing, metallographic testing, corrosion testing, WPS


Detil Peneliti

Dosen Pembimbing 1 :Moh. Miftachul Munir
Dosen Pembimbing 2 : Wiwik Dwi Pratiwi

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2009


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.