ANALISA PENGARUH VARIASI SUHU PEMANASAN PROSES STRAIGHTENING PADA BAGIAN WATER WALL PANEL TERHADAP NILAI KEKERASAN DAN STRUKTUR MIKRO

AN ANALYSIS OF THE INFLUENCE OF HEATING TEMPERATURE VARIETY OF STRAIGHTENING PROCESS IN WATER WALL PANEL TO THE VALUE OF HARDNESS AND MICRO STRUCTURE

Febryan Dionyda Valentin (6709040009)


Abstrak

Material SA 192 termasuk dalam material seamless carbon steel boiler tubes, dan sering digunakan untuk high-pressure service. Di PT. Dinamika Energitama Nusantara material SA 192 digunakan dalam pressure part boiler yaitu pada bagian water wall panel. Water wall panel memiliki dimensi cukup panjang, sehingga kemungkinan terjadi kelengkungan sangatlah besar. Kelengkungan bisa terjadi akibat thermal process atau defleksi yang diakibatkan pembebanan, oleh karena itu perlu dilakukan proses straightening. Dalam penelitian ini pemodelan menggunakan material SA 192 dengan dimensi 76,2 X 4,5 X 1000 dan SA 36 dengan dimensi 25,8 X 6 X 1000. Kelengkungan diroll dengan dimensi 20 mm dengan radius 6260 mm. Pemanasan dilakukan dengan suhu 450 C, 550 C, dan 650 C sebanyak 3 kali, kemudian diukur dimensi kelengkungannya. Selanjutnya dilakukan pengujian hardness dan struktur mikro. Sebagai pembanding dilakukan juga pengujian pada spesimen yang belum dilakukan pengerolan dan juga yang telah dilakukan pengerolan. ASME Sections II Part A menyebutkan material SA 192 dengan ketebalan kurang dari 5,1 mm, nilai kekerasannya tidak boleh melebihi 77 HRB (146 HVN). Dari hasil pengujian hardness didapatkan nilai kekerasan rata-rata pada material dengan suhu pemanasan 450 C sebesar 135 HVN di base metal dan 143 HVN di HAZ, pada material dengan suhu pemanasan 550 C sebesar 133 HVN di base metal dan 139 HVN di HAZ, sedangkan pada material dengan suhu pemanasan 650 C sebesar 130 HVN di base metal dan 136 HVN di HAZ. Ketiganya memenuhi persyaratan berdasarkan ASME Sections II Part A. Hasil foto mikro antara spesimen dengan suhu pemanasan 4500 C, 5500 C, dan 6500 C menunjukkan tidak adanya perbedaan yang signifikan. Kata kunci : boiler, water wall panel, straightening, nilai kekerasan, struktur mikro


Abstract

SA 192 material is included in seamless carbon steel boiler tubes material, and often be used to high-pressure service. In PT. Dinamika Energitama Nusantara, SA 192 material is used in pressure part boiler inside water wall panel. Water wall panel has long dimension enough, therefore it is possible to create curvature. Curvature is possibly happened because of the thermal process or deflection caused by imposition, so the straightening process needs to be done. In this study, the model used SA 192 material with 76,2 X 4,5 X 1000 dimension and SA 36 with 25,8 X 6 X 1000 dimension. The curvature was rolled with 20 mm dimension and 6260 mm radius. The heating was done under the temperature of 450 C, 550 C, and 650 C three times, and then the curvature dimension was measured. The next step was tested the unrolled specimens and the rolled specimens. ASME Sections II Part A mentioned that SA 192 material with less than 5.1 mm thickness, the value of hardness should not more than 77 HRB (146 HVN). The result of hardness test performed that the average value of hardness through a material with heating temperature of 450 C was 135 HVN in base metal and 143 HVN in HAZ, for the material with heating temperature of 550 C was 133 HVN in base metal and 139 HVN in HAZ, whilst for the material with heating temperature of 650 C was 130 HVN in base metal and 136 HVN in HAZ. Those three results filled the requirements based on the ASME Sections II Part A. The micro picture showed that there was no significant different among specimens with heating temperature of 450 C, 550 C, and 650 C. Keywords : boiler, water wall panel, straightening, value of hardness, micro structure


Detil Peneliti

Dosen Pembimbing 1 :Usman Dinata
Dosen Pembimbing 2 : Muhamad Ari

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2009


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.