ANALISA PENGELASAN PADA MATERIAL SA-335 P 11 DENGAN SA-240 TP 304L MENGGUNAKAN VARIASI ELEKTRODA E308L, E309L, DAN E312 TERHADAP SIFAT MEKANIKNYA PADA SUPPLY STEAM BOILER DI PT. PETROKIMIA GRESIK

ANALYSIS OF WELDING MATERIAL SA335 P 11 WITH SA240 TP 304L ELECTRODE USING VARIATIONS E308L, E309L, AND E312 OF MECHANICAL PROPERTIES ON SUPPLY STEAM BOILER IN PT. PETROKIMIA GRESIK

Iffad Rakhmanhuda (6709040008)


Abstrak

PT. Petrokimia Gresik, perusahaan yang bergerak di dalam bidang produksi pupuk, bahan kimia, tangki, dll. Dari berbagai macam jenis alat dan media yang digunakan untuk proses produksi, salah satunya yaitu supply steam boiler, yaitu salah rangkaian pipa penyalur uap yang berfungsi untuk menyuplai uap panas hasil pemanasan boiler ke berbagai penjuru pabrik. Pipa penyalur uap tersebut menggunakan material low alloy steel Penelitian dilakukan dengan melakukan variasi elektroda SMAW yaitu, elektroda E308L, E309L, dan E312, sebagai variabelnya. Kemudian dilakukan pengujian menggunakan uji kekerasan, uji tarik dan uji tekuk serta uju makro dan mikro bertujuan untuk mengetahui sifat mekanik yang terjadi setelah dilakukan pengelasan. Setelah dilakukan pengujian untuk menganalisa sifat mekanik dan struktur yang terbentuk melalui variasi 3 elektroda didapat hasil pengujian makro memiliki penembusan 2,3 ? 3,00 mm. Pengujian mikro di weld metal menunjukkan elektroda E309L memiliki grain size yang lebih besar dibanding elektroda lainnya. Lalu dari hasil pengujian tensile E308L memiliki nilai sebesar 67600 psi, E309L sebesar 71605 psi, dan E312 sebesar 71971 psi. dari pengujian bending tidak ditemukan defect apapun. Kemudian semua nilai pengujian hardness memenuhi code ASME Sec IX yakni sebesar 210 HVN kecuali weld metal pada elektroda E312 yang memiliki nilai kekerasan 233 HVN. Sehingga penggunaan elektroda E308L dan E309L sudah cukup memenuhi semua kriteria. Kata kunci : SMAW,Supply Steam boiler, Problem Steel, dan Defect


Abstract

PT. PKG, a company engaged in the production of fertilizers, chemicals, tanks, etc. From various types of devices and media used for the production process, one of which supply steam boiler, which is one of a series of steam conduit that serves to supply steam heating boiler to various parts of the factory. The steam conduit use low alloy steel material Research conducted by the variation of SMAW electrodes, electrode E308L, E309L, and E312, as variables. Then be tested using a hardness test, tensile test and bending test as well as macro and micro test to determine the mechanical properties that occur after welding. After testing to analyze the mechanical properties and structure of the electrode 3 is formed through variation of the test results obtained macro has breakout from 2.3 to 3.00 mm. Tests showed micro electrode E309L weld metal has a larger grain size than the other electrode. From the tensile test results E308L has a value of 67600 psi, E309L at 71 605 psi, and the E312 at 71 971 psi. of bending test not found any defect. Then the value of hardness testing meets ASME Sec IX, amounting to 210 HVN except E312 weld metal on the electrode which has a hardness value of 233 HVN. So the use of electrode E308L and E309L has fulfilled all the criteria. Keyword: SMAW,Supply Steam boiler, Problem Steel, dan Defect


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : Ruddianto

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2009


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.