PENGARUH INTERPASS TEMPERATURE PENGELASAN HARD FACING CARBON STEEL 283 GR C DAN HARDOX 400 PADA COVER FLIGHT BEARING TERHADAP KEKERASAN DAN STRUKTUR MIKRO

EFFECT OF INTERPASS TEMPERATURE HARD FACE WELDING ON CARBON STEEL 283 GR C AND HARDOX 400 APPLICABLE TO COVER FLIGHT BEARING VALUED WITH HARDNESS VICKERS AND MICROSTRUCTURES

David Setyo Pramono (6709040007)


Abstrak

Conveyor adalah teknologi yang selalu digunakan pada pabrik-pabrik besar khususnya yang bergerak di bidang produksi untuk memuat barang belum jadi, setengah jadi dan hasil produksi. Dan tentunya ada bahan mentah yang diangkut melalui kapal diperlukan penghubung antara conveyor dan kapal yaitu screw conveyor. Pada srew conveyor terdapat bagian yang juga sangat penting yaitu cover flight bearing. Gesekan yang terjadi antara kedua bagian tersebut merupakan permasalahan yang sering terjadi disebabkan oleh keausan pada area permukaan. Pengelasan hard facing merupakan salah satu metode untuk melapisi permukaan agar tahan terhadap keausan. Penelitian ini membahas pengaruh interpass temperatur pengelasan hard facing Carbon Steel A 283 Gr C dan Hardox 400 terhadap kekerasan dan struktur mikro dari cover flight bearing. Pengelasan hard facing dilakukan dengan menggunakan proses pengelasan SMAW posisi 1G. Sebelum pengelasan, dilakukan proses preheat dengan temperatur 200OC terlebih dahulu. Standard jumlah layer pada hard facing adalah 3 layer, pada proses pengelasannya setiap layer dilakukan interpass temperature yang berbeda yaitu suhu 100OC, 300OC dan 500OC. Untuk mengetahui perubahan struktur mikro maka dilakukan pengujian metalografi menggunakan mikroskop optik dengan pembesaran 200X,500X dan 1000X. Sedangkan untuk mengetahui nilai kekerasannya maka dilakukan pengujian hardness Vickers dengan beban uji yang dipakai adalah 10kg dan ditekan selama 10 detik. Penelitian ini dapat membuktikan bahwa Interpass temperature 100OC menghasilkan nilai kekerasan paling tinggi dibandingkan dengan interpass temperature 300OC dan 500OC. Pada daerah HAZ nilai kekerasan Hardox 400 yaitu 277 HVN lebih besar dibandingkan pada carbon steel A283 Gr C yang memiliki kekerasan 159 HVN.


Abstract

Conveyor is a technology used at strategic factory especially withstand on production site for unfinishes goods loading process, half ? finish, and final production. Absolutely, there are any raw material to load by ship connector needed between conveyor and ship itself, the connector part are named screw conveyor. At screw conveyor, there are an importance section, the part is cover flight bearing. A friction that occur between that both parts constitute problem may often caused by worn out at surface area. Hard face welding is one of method for cladding material surface in order to worn out resist. This research is studying about interpass temperature by welding with hard facing method on Carbon Steel A 283 Grade C and Hardox 400 to hardness value and microstructures at cover flight bearing part. Hard face welding is doing by SMAW process with 1G position. Before welding conducted, preheat process has doing with temperature about 200 degree Celcius. Standard of layer amount on hard facing are 3 layers, at the process in each layer is doing with different interpass temperature 100OC, 300OC and 500OC. To knowing any changes on microstructures so metallography test are needed using the microscope optic with zooming 200X,500X and 1000X. Beside that to knowing hardness value so hardness vickers are needed using 10kg load test and pressed until 10 seconds. This study is proofing, at interpass temperature 100 degree Celcius have the highest hardness Vickers value comparing to interpass temperature 300 degree celcius and 500 degree celcius. At the heat affected zone, hardness vickers value Hardox 400 is 277 HVN higher than hardness value at carbon steel A 283 Grade C in actually has a hardness Vickers value 159 HVN.


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 : Rasiawan

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2009


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.