STUDI PENGELASAN STAINLESS STEEL SA 240 TYPE 304 MENGGUNAKAN GMAW MODE COLD ARC DIBANDINGKAN DENGAN GTAW

STUDY OF WELDING STAINLESS STEEL SA 240 TYPE 304 USING GMAW COLD ARC MODE COMPARED WITH GTAW

Dika Anggara (6709040003)


Abstrak

Pengelasan GMAW (Gas Metal Arc Welding) secara umum memiliki beberapa tipe metal transfer diantaranya yaitu short circuit, globular transfer, spray transfer dan pulse arc. Dari keempat mode tersebut muncul mode baru hasil pengembangan dari short-circuit transfer yang dinamakan cold arc. Cold arc bertujuan menciptakan pengelasan dengan kualitas yang lebih baik dari segi penembusan khususnya pada bagian akar las. Dengan masukan panas yang relatif rendah dan waktu yang lebih cepat menjadi nilai tambah dari mode baru ini.Tujuan penelitian ini adalah membandingkan hasil pengelasan GMAW mode cold arc dan GTAW pada bagian akar las pada material stainless steel SA 240 type 304 yang divariasikan 0 mm (tanpa gap), 2 mm, dan 4 mm. Dari hasil pengujian visual didapatkan bahwa kualitas hasil pengelasan GMAW mode cold arc memiliki deformasi yang lebih kecil dibandingkan hasil pengelasan GTAW. Percikan yang terjadi pun hampir tidak ada pada kedua proses pengelasan. Dari hasil pengujian radiografi, GMAW mode cold arc memilik cacat porositas lebih sedikit dibandingkan GTAW. Hasil makro etsa menunjukkan penembusan yang terjadi pada GMAW mode cold arc sebesar 3,5 mm sedangkan pada GTAW sebesar 2,5 mm. Hasil uji lengkung (bending) menunjukkan keberterimaan pada semua spesimen kecuali pada GMAW gap 0 mm (tanpa gap) dan GTAW gap 0 mm (tanpa gap). Dari hasil mikro etsa dihitung kandungan ferrite yang terjadi yaitu sebesar 10,5 % sampai 29,29 %. Dari keseluruhan hasil pengujian, GMAW mode cold arc memiliki kualitas lebih baik dibandingkan GTAW. Sehingga jika diterapkan pada suatu pekerjaan, akan memberikan keuntungan pada segi efisiensi dan efektifitas biaya pengelasan. Kata kunci: GMAW, Cold arc, GTAW, Gap


Abstract

Welding GMAW (Gas Metal Arc Welding) generally have some type of metal transfer among short circuit, globular transfer, spray arc transfer and pulse. The fourth mode of the emerging new mode of the development of short-circuit transfer arc called cold arc. Cold arc welding with the aim to create a better quality in terms of penetration especially in the weld root. With a relatively low heat input and a faster time to be additional- value of this new mode.The purpose of this study was to compare the results of arc welding GMAW and GTAW cold mode at the root of the weld material SA 240 stainless steel type 304 is varied 0 mm (no gap), 2 mm, and 4 mm. Results of the visual examination showed that the quality of the welding arc GMAW cold mode has a smaller deformation compared to the GTAW welding. Spatter that happened was almost non-existent in both the welding process. Results of the radiographic examination, pick the arc GMAW cold mode porosity defects less than GTAW. Macro-etching results showed that penetration occurred in cold mode GMAW arc of 3.5 mm and in GTAW of 2.5 mm. Bend test results show acceptance on all specimens except GMAW gap 0 mm (no gap) and GTAW gap 0 mm (no gap). Calculated from the results of micro-etching ferrite content occurred, ie by 10.5% to 29.29%. From the overall results of the test, GMAW arc cold mode has better quality than the GTAW. So that when applied to a job, will give you an advantage in terms of efficiency and cost effectiveness of welding. Key words: GMAW, Cold arc, GTAW, Gap


Detil Peneliti

Dosen Pembimbing 1 :Soeweify
Dosen Pembimbing 2 : Muhamad Ari

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2009


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.