PENGARUH VARIASI KADAR FOSFAT TERHADAP KEKUATAN MEKANIK DAN SIFAT KETAHANAN API PADA KOMPOSIT GEOPOLIMER BERSERAT

THE EFFECT OF PHOSPHATE VARIATION TOWARD MECHANICHAL STRENGTH AND FIRE RESISTANCE OF COMPOSITE FIBROUS GEPOLYMER MATERIAL

Muhammad Rizqy Dailami (6611040025)


Abstrak

PENGARUH VARIASI KADAR FOSFAT TERHADAP KEKUATAN MEKANIK DAN SIFAT KETAHANAN API PADA KOMPOSIT GEOPOLIMER BERSERAT Oleh : M.Rizqy Dailami NRP. 6611 040 025 Pembimbing: 1. Ir. Wiwik Dwi Pratiwi, MT. 2. Rizal Indrawan, S.ST., MT. ABSTRAK Papan geopolimer berserat terbuat dari komposit geopolimer dengan penambahan serat PP dan fosfat diharapkan lebih kokoh, tahan terhadap benturan, juga tahan terhadap api/suhu tinggi. Geopolimer merupakan suatu material berupa polimer anorganik alumino silikat dengan rantai Si-O-Al yang disintesis dari material pozzolan yang kaya akan silika dan alumina dengan larutan pengaktif natrium hidroksida dan bahan pengikat sodium silikat. Penambahan variasi kadar fosfat dilakukan untuk mengetahui berapa kadar fosfat yang sesuai jika papan geopolimer berserat ini diaplikasikan sebagai panel pemisah ruangan. Variasi pembanding fosfat yang dilakukan adalah Si/P 0, Si/P 30, Si/P 50, dan Si/P 70, dan komposisi serat PP 1,5% volum. Setelah dilakukan pengujian mekanik dan tahan api didapatkan hasil yaitu papan yang sesuai untuk diaplikasikan sebagai papan geopolimer fosfat adalah geopolimer dengan penambahan Si/P 50 karena memiliki nilai kuat tarik paling tinggi sebesar 1,92 MPa. Nilai kuat patah sebesar 6,203 N dan defleksi sebesar 0,315 mm. Tingkat kevalidan untuk perbandingan defleksi dengan software NASTRAN mencapai 85% . Untuk uji ketahanan api yang berdasarkan ketentuan ASTM D635 spesimen ini termasuk spesimen yang tahan bakar. Kata kunci : Geopolimer, fosfat, serat PP


Abstract

THE EFFECT OF PHOSPHATE VARIATION FOR MECHANICHAL STRENGTH AND FIRE RESISTANCE OF COMPOSITE FIBROUS GEPOLYMER MATERIAL By : M.Rizqy Dailami NRP. 6611 040 025 Advisor: 1. Ir. Wiwik Dwi Pratiwi, MT. 2. Rizal Indrawan, S.ST., MT. ABSTRACT Geopolymer fibrous board was made of geopolymer composites with the addition of PP fibers and phosphate that expected to be more strength, impact resistant, and also fire resistance. Geopolymer is an inorganic polymer material in form of alumino silicates with chain Si-O-Al. Synthesized from pozzolan material which is rich in silica and alumina with an activator of sodium hydroxide and sodium silicate. The addition of more variation levels of phosphate was held to find out the appropriate levels of phosphate if this geopolymer fibrous board applied as panel room separator. The variations comparison of phosphate that have been done are Si/P 0, Si/P 30, Si/P 50, and Si/P 70, and the composition of PP fiber composition 1,5% by volume. After the testing of mechanical and fire resistant test is done, the result which is suitable to be applied as a phosphate geopolymer board is geopolymer with the addition of Si/P 50 because it has the highest tensile strength that is 1,92 MPa. Flexural strength that is 6,203 N and the deflection that is 0,315 mm. The level of validity compare the deflection with NASTRAN software has reached 85%. For fire resistance test, based on standart of ASTM D635 this specimen includes to fire resistance specimen. Key words : Geopolymer, phosohate, PP fiber


Detil Peneliti

Dosen Pembimbing 1 :Wiwik Dwi Pratiwi
Dosen Pembimbing 2 : Rizal Indrawan

Program Studi : D4 - TEKNIK DESAIN DAN MANUFAKTUR
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.