ANALISIS PERBANDINGAN JENIS SERAT TERHADAP SIFAT MEKANIK PAPAN GEOPOLIMER BERSERAT DENGAN METODE ELEMEN HINGGA

KIND COMPARISON ANALYSIS OF FIBER TO MECHANICAL CHARACTERISTIC OF FIBROUS GEOPOLYMER BOARD USING FINITE ELEMENT METHOD

Yanuar Triadi (6611040001)


Abstrak

ABSTRAK ANALISIS PERBANDINGAN JENIS SERAT TERHADAP SIFAT MEKANIK PAPAN GEOPOLIMER BERSERAT DENGAN METODE ELEMEN HINGGA Oleh : Yanuar Triadi NRP. 6611040001 Geopolimer merupakan suatu material berupa polimer anorganik aluminosilikat dengan rantai Si-O-Al yang disintesis dari material pozzolan yang kaya akan silika dan alumina dengan larutan pengaktif natrium hidroksida dan bahan pengikat Na silikat. Dengan penambahan serat pada geopolimer yang berfungsi sebagai pengisi dan penguat menghasilkan sifat geopolimer berserat menjadi lebih baik. Analsis perbandingan jenis serat terhadap sifat mekanik papan geopolimer berserat dilakukan untuk mengetahui jenis serat yang sesuai untuk diaplikasikan sebagai papan penyekat ruangan. Dengan komposisi serat 1,5% volume, variasi jenis serat yang digunakan adalah serat polypropylene, serat polyvinyl alcohol, serat kenaf dan tanpa serat sebagai pembandingnya. Serta analisis menggunakan software berbasis metode elemen hingga diharapkan mampu mengetahui struktur kekuatan tegangan dari papan geopolimer berserat dengan hasil yang mendekati pada kenyataan. Hasil dari penelitian, perbandingan nilai deformasi dari analisa menggunakan software Nastran dengan uji fleksural diperoleh nilai deformasi pada geopolimer berserat kenaf sebesar 0,450 mm dan 0,529 mm. Dan untuk nilai standar papan gipsum konfensional memiliki rata-rata nilai deformasi sebesar 0,545 mm. Maka dari itu, papan geopolimer dengan penambahan serat kenaf layak untuk dijadikan papan penyekat ruangan. Kata kunci : Geopolimer, Jenis Serat, Metode Elemen Hingga


Abstract

ABSTRACT KIND COMPARISON ANALYSIS OF FIBER TO MECHANICAL CHARACTERISTIC FIBROUS GEOPOLYMER BOARD USING FINITE ELEMENT METHOD By : Yanuar Triadi NRP. 6611040001 Geopolymer is a material such as aluminosilicate inorganic polymer with chain Si-O-Al were synthesized from pozzolan material which is rich in silica and alumina with an activator solution of sodium hydroxide and Na silicate binder. With the addition of fiber to the geopolymer which serves as a reinforcing filler and produce geopolymer fibrous nature to be better. The analysis comparison of the type of fiber on mechanical properties of geopolymer fiber board conducted to determine the types of fibers suitable to be applied as a room divider board. With the fiber composition of 1.5% by volume, variations in the type of fiber used is a polypropylene fiber, polyvinyl alcohol fiber, kenaf fiber as a fiber and without comparison. As well as software-based analysis using the finite element method is expected to know the voltage of the power structure of fibrous geopolymer board with results closer to reality. Results of the research, a comparison of the value of the deformation of the analysis using Nastran software with flexural test deformation values obtained on geopolymer kenaf fiber of 0.450 mm and 0.529 mm. And to standard values conventional gypsum board has an average value of deformation of 0.545 mm. Therefore, the board geopolymer with the addition of kenaf fiber suitable as a room divider board. Keyword : Geopolymer, Fiber type, Finite Element Method


Detil Peneliti

Dosen Pembimbing 1 :Wiwik Dwi Pratiwi
Dosen Pembimbing 2 : Rizal Indrawan

Program Studi : D4 - TEKNIK DESAIN DAN MANUFAKTUR
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.