PERENCANAAN MATERIAL SARUNG TANGAN TAHAN TERHADAP SUHU TINGGI (STUDI KASUS: HOT WORKING PADA PT.X

SAFETY GLOVES MATERIAL PLAN FOR HIGH TEMPERATURE RESIST. (STUDY CASE: HOT WORKING AT PT.X

Sinatrio Dawam Muslim (6512040078)


Abstrak

Sarung tangan merupakan salah satu alat pelindung diri (APD) yang sering digunakan pada setiap pekerjaan. Sarung tangan mempunyai kegunaan untuk mengurangi angka kecelakaan kerja, dimana pada proses pekerjaan 3 LPE pelapisan bagian luar pipa dengan menggunakan 3 layer polyethylene. Proses pelapisan tersebut menggunakan alat Extruder dengan memanaskan material PE, FBE dan polyethylene sampai menghasilkan temperatur sekitar 180-240oC. Kondisi aktual sarung tangan yang dimiliki perusahaan tidak mampu menahan suhu 180-240 oC, banyak pekerja mengalami kecelakaan luka bakar pada tangan. Penelitian ini termasuk penelitian reaserch and development dimana penelitian ini ingin meneliti dan mengembangkan material baru yang digunakan pada sarung tangan. Oleh karena itu kedepannya diharapkan sarung tangan ini mampu menahan suhu tinggi. Sarung tangan yang dimiliki perusahaan dan material sarung tangan yang digunakan akan melalui tahap pengujian perpindahan panas dengan hasil sebagai berikut material yang terdapat pada sarung tangan memiliki 2 lapisan yaitu material kulit dan cutton. Thermoselector yang digunakan sebanyak 3 yaitu T1, T5, T6. T1 merupakan lokasi pengukuran paling atas dibagian material kulit atau kontak dengan panas, T5 merupakan lokasi pengukuran dibagian tengah antara material kulit dan cutton, T6 merupakan lokasi pengukuran paling bawah dibagian cutton. Pengujian ini mengambil data penurunan suhu yang dihasilkan per 5 detik ( oC). T1= 199 (5 detik), 200 (10 detik), 200 (15 detik), 200 (20 detik). T5= 175 (5 detik), 178 (10 detik), 182 (15 detik), 185 (20 detik). T6= 137 (5 detik), 139 (10 detik), 142 (15 detik), 147 (20 detik). Sedangkan pada material baru yang digunakan memiliki banyak lapisan yaitu lapisan material 8 (sandwich), lapisan 4 kevlar, 7 alumina powder, dan 4 kulit. Pada tahap pengujian kedua ini mengambil data penurunan suhu yang dihasilkan per 5 detik ( oC). T1= 199 (5 detik), 200 (10 detik), 200 (15 detik), 200 (20 detik). T5= 64 (5 detik), 67 (10 detik), 72 (15 detik), 74 (20 detik). T6= 59 (5 detik), 63 (10 detik), 66 (15 detik), 68 (20 detik). Berdasarkan hasil tersebut dapat diketahui bahwa penambahan alumina yang lebih banyak mampu menurunkan suhu dengan efektif dalam waktu paparan 5 detik. Dapat disimpulkan bahwa komposisi material 8 dapat direkomendasikan sebagai bahan untuk pembuatan sarung tangan tahan panas untuk pekerjaan 3 LPE yang memiliki suhu 1800C ? 2400C. Kata kunci: 3 LPE, FBE (Fusion Bonded Epoxy), polyethylene, Extruder, Thermoselector, sandwich


Abstract

Glove is one of the personal protective equipment (PPE) that is used frequently on every job. Glove has utility to reduce the number of accident at work, which in the process of 3 LPE work coating the outer part of the pipe by using 3 layer polyethylene. The coating process used Extrude equipment by heating the PE material, FBE and polyethylene until generate the temperature for about 180-240 ? C. The actual condition of the glove which company has is unable to hold the temperature of 180-240?C, many employees had burn accident to the hand. This study is included research and development study where this research was to examine and develop new materials used in making glove. Accordingly the glove is expected to be able to hold high temperature. The glove which company has and the glove material will be through the heat transfer testing phase with the following result, the material contained on the glove should has two layers of material, namely leather and cutton. There are three Thermoselector being used, namely T1, T5, T6. T1 is the upper location of measurement in the part of leather material or contact with the heat, T5 is the middle location of measurement between the leather material and cutton, T6 is the bottom location of measurement in cutton part. This test retrieved the data from decrease in temperature which taken per 5 seconds (oC). T1 = 199 (5 seconds), 200 (10 seconds), 200 (15 seconds), 200 (20 seconds). T5 = 175 (5 seconds), 178 (10 seconds), 182 (15 seconds), 185 (20 seconds). T6 = 137 (5 seconds), 139 (10 seconds), 142 (15 seconds), 147 (20 seconds). Meanwhile the new material being used has many layers that is layer of 8 materials (sandwich), 4 kevlar layer, 7 alumina powder, and 4 leather. The second test took the data of decrease in temperature which taken per 5 seconds (oC). T1 = 199 (5 seconds), 200 (10 seconds), 200 (15 seconds), 200 (20 seconds). T5 = 64 (5 seconds), 67 (10 seconds), 72 (15 seconds), 74 (20 seconds). T6 = 59 (5 seconds), 63 (10 seconds), 66 (15 seconds), 68 (20 seconds). Based on the results mentioned above,it can be seen that the adding more alumina is able to decrease the temperature effectively within 5 seconds of exposure. It can be concluded that the composition materials 8 can be recommended as an ingredient for the manufacture of heat-resistant glove for 3 LPE work which has temperature of 180? C - 240? C. Keyword: 3 LPE, FBE (Fusion Bonded Epoxy), polyethylene, Extruder, Thermoselector, sandwich


Detil Peneliti

Dosen Pembimbing 1 :Arief Subekti
Dosen Pembimbing 2 : George Endri K

Program Studi : D4 - TEKNIK KESELAMATAN DAN KESEHATAN KERJA
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.