ANALISA CACAT HASIL PENGELASAN PIPA 4 INCH SS-400 CARBON STEEL MENGGUNAKAN METODE RADIOGRAFI TEST

DEFECT ANALYSIS OF WELDING PIPE 4 INCH SS400 USING CARBON STEEL RADIOGRAPHY TEST

Refa Pedi Utama Putra (6313030040)


Abstrak

Baja menjadi material yang sering digunakan dalam bidang kontuksi. Karena baja memiliki sifat yang kuwat, daktilitas tinggi, tidak mudah korosi dan memilki sifat elastisitas yang cukup tinggi. Dalam proses pengerjaan kontruksi baja seperti sambungan pipa pastinya tidak terlepas dari proses inspeksi pengelasan. Proses inspeks dari pengelasan merupakan bagian penting dalam pengerjaan proyek kontruksi. Inspeksi menggunakan metode Radiografi Test ( RT ) yang merupakan proses inspeksi yang tergolong NDT ( Non Destructive Test) pengujian yang tanpa merusak material. Tugas akhir ini bertujuan untuk mengetahui cacat pengelasan pada pipa 4 inch ss-400 carbon steel menggunakan metode Radiografi Test. Setelah dilakukan Radiografi Test menganalisa hasil cacat pad alas pipa 4 inch ss-400 carbon steel menurut standart dari ASME section IX, serta cara melakukan repair sambungan pengelasan berdasarkan ASME section IX. Bedasarkan hasil pengujan Radiografi Test pada sambungan pengelasan pipa 4 inch ss-400 carbon steel terdapat cacat. Dari hasil film radiografi mempunyai indikasi Incomplete Penetration dengan panjang indikasi 30 mm dan 50 mm, karena panjang indikasi melebihi batas yang ditentukan oleh ASME section IX maka sambungan pengelasan perlu dilakukan repair. Kata kunci : Carbon Steel, Non Destructive Test


Abstract

Steel into a material that is often used in the construction field. Because steel has strength, high ductility, not easy to corrosion and have the properties of elasticity is high enough. In the process of construction such as steel pipe joints certainly can not be separated from the process of welding inspection. The inspection process at the welding is an important part in the execution of construction projects. Inspection methods Test Radiography (RT) which is an inspection process that pertained NDT (Non Destructive Test) testing without damaging material.Inspeksi using Test Radiography (RT) which is an inspection process that pertained NDT (Non Destructive Test) testing without damage material. This final project aims to determine welding defects in the pipe 4 inch ss-400 carbon steel using methods Radiografi Test. After analyzing the results of defects Radiography Test pad pedestal 4 inch pipe ss-400 carbon steel according to the standards of the ASME section IX, as well as how to do repair welding connection by ASME section IX. Based on test results Radiography Test on the connection pipe welding ss-400 4-inch carbon steel there are defects. From the results of radiographic film has indications Incomplete Penetration with long indication of 30 mm and 50 mm, since the length of indications exceeds the limit specified by ASME section IX of the welding connection is necessary to repair. Keywords: Carbon Steel, Non Destructive Test


Detil Peneliti

Dosen Pembimbing 1 :Pekik Mahardhika
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK PERMESINAN KAPAL
Angkatan : 2013


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.