ANALISA PERBANDINGAN KOMPOSISI MATERIAL PENGGANTI PISTON RING TERHADAP KOMPOSISI MATERIAL STANDART PADA KOMPRESOR K-102 OLEH PENGARUH (H2S) DI PT. ALP PETRO INDUSTRY

ANALYSIS COMPARATIVE OF THE MATERIAL COMPOSITION OF THE PISTON RING REPLACEMENT THE COMPOSITION OF THE MATERIAL STANDARD K-102 COMPRESSOR BY THE EFFECT H2S in PT. ALP PETRO INDUSTRY

Abdullah Latif Udaibi (6312030035)


Abstrak

ANALISA PERBANDINGAN KOMPOSISI MATERIAL PENGGANTI PISTON RING TERHADAP KOMPOSISI MATERIAL STANDART PADA KOMPRESOR K-102 OLEH PENGARUH H2S DI PT. ALP PETRO INDUSTRY Nama Mahasiswa : Abdullah Latif Udaibi NRP : 6312030035 Jurusan : Teknik Permesinan Kapal, PPNS Dosen Pembimbing : Subagio So?im, ST, MT ABSTRAK Kompresor merupakan alat yang berfungsi untuk meningkatkan / memampatkan tekanan fluida yang berupa gas. Di PT. ALP Petro Industri terdapat sebuah kompresor K-102 yang berfungsi untuk mensirkulasikan gas hidrogen yang melewati reaktor demitalizing dan refining. Pengujian komposisi material dilakukan dengan menggunakan pengujian EDX, sehingga dapat diketahui perbedaan tinggi rendahnya persentase komposisi material piston ring pengganti. Pengujian ini dilakukan untuk mengetahui komposisi material, dikarenakan jenis material tidak ada di dalam manual book. Setelah dilakukan perhitungan laju korosi, dapat diketahui bahwa persentase kandungan kimia pada material pengganti piston ring lebih tinggi dibandingkan material standart piston ring yang sudah digunakan. Dari perhitungan laju korosi dapat diketahui nilai laju korosi pada material pengganti sebesar 0,82 mm/yr, dan nilai laju korosi pada material standart 1,076 mm/yr, maka termasuk dalam kategori fair masih bisa digunakan. Dengan perhitungan remaining life time dapat diketahui umur material pengganti piston ring 6,3 tahun dan umur material standart piston ring 4,8 tahun, Sehingga life time material pengganti piston ring K-102 lebih lama dibandingkan material standart dan dapat menghemat biaya penggantian material piston ring. Kata-kata kunci : kompresor K-102, demitalizing dan refining, corrosion induced Hydrogen, piston ring.


Abstract

ANALYSIS COMPARATIVE OF THE MATERIAL COMPOSITION OF THE PISTON RING REPLACEMENT THE COMPOSITION OF THE MATERIAL STANDARD K-102 COMPRESSOR BY THE EFFECT H2S in PT. ALP PETRO INDUSTRY Name : Abdullah Latif Udaibi NRP : 6312030035 Department : Teknik Permesinan Kapal, PPNS Counsellor Lecturer : Subagio So?im, ST, MT ABSTRACT Compressor is a tool that serves to increase / compress the fluid pressure in the form of gas . In PT . ALP Petro Industry there is a compressor K - 102 which is used to circulate hydrogen gas through the reactor demitalizing and refining. Material composition testing done using EDX testing , so that can know the difference of high and low percentage of the material composition of the piston ring replacement. This test was conducted to determine the composition of the material , due to the type of material is not in the manual book. After analysis of material composition and calculation of the rate of corrosion , it can be seen that the percentage content of the material replacement piston ring more than the standard piston ring material that has been used. By calculating the rate of corrosion can be seen on the material value of corrosion rate of 0,82 mm replacement / yr , and the value of the rate of corrosion of the material standard of 1,076 mm / yr , it is included in the category of fair still useable. By calculating remaining life time can be known age replacement material piston ring material life of 6,3 years and 4,8 years standard piston ring . So that the life time replacement material piston ring K - 102 longer than the standard material and can save the cost of replacing the piston ring material Kyword : Compressor K-102, demitalizing dan refining, corrosion induced Hydrogen, Piston ring.


Detil Peneliti

Dosen Pembimbing 1 :Subagio Soim
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK PERMESINAN KAPAL
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.