ANALISA PERBANDINGAN KEKUATAN MATERIAL PENGGANTI DAMPER PLATE TERHADAP MATERIAL ORIGINAL PADA RECYCLE COMPRESSOR K-102

COMPARISON ANALYSIS of MATERIAL STRENGTH as an alternate of DAMPER PLATE against original material ON RECYCLE COMPRESSOR K-102

Reandy Risky Virnanda (6311030055)


Abstrak

Kompresor merupakan alat yang berfungsi meningkatkan tekanan fluida yang berupa gas. Pada equipment di Re-Refining and Blending Plant PT ALP Lubrindo Pratama terdapat recycle compressor yang digunakan untuk menjaga aliran fluida tidak kurang dari 250 kg/hr. Pada recycle compressor terdapat katup sisi keluar yang didalamnya terdapat komponen damper plate. Damper Plate berfungsi untuk mencegah terjadinya kebocoran yang dapat menyebabkan pressure drop. Kasus yang terjadi di lapangan adalah damper plate yang sering patah dan menyebabkan produksi menurun akibat harus dimatikannya kompresor selama proses maintenance. Penyebab terjadinya patah pada komponen ini adalah penggantian material damper plate yang tidak sesuai dengan standard. Sehingga perlunya dilakukan pengujian kekuatan tarik dan komposisi material sebagai perbandingan kualitas damper plate pengganti terhadap damper plate standard Dari hasil analisa damper plate pengganti memiliki kekuatan tarik yaitu 1454,75 N/mm2 sedangkan damper plate standard memiliki kekuatan tarik sebesar 1270 N/mm2. Ditinjau dari komposisi kimia yang ada damper plate pengganti memiliki jumlah unsur Fe 2% lebih banyak dan memiliki kandungan unsur Cr 16% lebih sedikit dari damper plate standard. Dari hasil evaluasi damper plate pengganti akan mengalami kerusakan lebih cepat disebabkan kandungan unsur Fe yang banyak yang akan mempercepat proses korosi logam damper plate akibat dari kandungan gas kompresor yang bersifat korosif yaitu gas H2S.


Abstract

Compressor is a tool that serves to increase fluid pressure in the form of gas. In Re-Refining and Blending Plant PT ALP Lubrindo Pratama there are one equipment called recycle compressor which use to hold fluid pressure not less than 20 kg/hr. One of the spare part on recycle compressor is damper plate which install in the valve discharge. This damper plate is prevent leak from valve which can make pressure drop. The problem in the plant is damper plate break and make the production is drop because recycle compressor must be shutdown under maintenance. Cause of this problem is replacement material of damper plate which not original because the original part of damper plate is not sell in Indonesian. From the results of analysis of damper plate replacement material namely have the power of 1454,75 N/mm2 while the damper plate standard material has the power of 1270 N/mm2. In terms of chemical composition which is a replacement plate damper has a number of elements of Fe 2% more and have the content of element Cr 16% fewer than the damper plate standard. From the results of the evaluation of damper plate replacement will damage more quickly due to the content of element Fe much will accelerate the process of corrosion of metal damper plate due to the womb of gas compressor which are corrosive gas H2S.


Detil Peneliti

Dosen Pembimbing 1 :Pranowo Sidi
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK PERMESINAN KAPAL
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.