ANALISA KEKERASAN BAJA KARBON RENDAH ST 41 SETELAH MENGALAMI PROSES HOT DIPPED GALVANIZE DENGAN VARIASI KETEBALAN

ANALYSIS OF LOW CARBON STEEL HARDNESS ,ST 41, AFTER HOT DIPPED GALVANIZED PROCESS WITH VARIOUS

Ach. Khoiri Hidayat (6311030031)


Abstrak

Baja merupakan material logam yang banyak digunakan di bidang teknik. Baja mempunyai beberapa keunggulan di bandingkan bahan konstruksi lainnya, merupakan material yang mempunyai sifat keras dan ulet. Namun sering kali hal ini tidak ditunjang dengan ketahanan korosi yang memadai, sehingga perlu dilakukan suatu inovasi dalam menanggulangi permasalahan tersebut. Dengan melakukan proses surface treatment yaitu melapisi perlindungan pada permukaan logam dengan logam lain, salah satunya dengan cara Hot Dipped Galvanize. Proses pelapisan hot dipped galvanize akan membuat permukaan material semakin tebal sehingga mempengaruhi sifat kekerasan material. Oleh sebab itu maka perlu dilakukan analisa pengaruh galvanisasi terhadap kekerasan suatu material dengan menggunakan pengujian destructive test. Yaitu pengujian dengan cara merusak material namun bertujuan untuk mengetahui kekuatan dan sifat mekanik material. Pada penelitian ini material baja karbon rendah ST 41 akan diuji dengan menggunakan pengujian kekerasan (hardness test). Hal ini bertujuan untuk mengetahui berapa nilai kekerasan yang dapat diketahui dari perbedaan ketebalan lapisan galvanis pada material sehingga diketahui nilai hardness material dengan pengaruh ketebelan lapisan galvanis yang berbeda. Kata Kunci : Hot Dipped Galvanize, Hardness Test, ST 41


Abstract

Steel is a metal material that is widely used in engineering. Steel has several advantages compared to other construction materials, a material that has properties of hard and tenacious. But too often this is not supported by sufficient corrosion resistance, so we need some innovation in tackling these problems. By performing surface treatment process that coats the protection of metal surfaces with other metals, such as by Hot Dipped Galvanizing. Hot dipped galvanized coating process would make the thicker the material surface properties that affect the hardness of the material. Therefore it is necessary to analyze the effect of galvanizing the hardness of a material by using destructive testing test. That is how destructive material testing but aims to determine the strength and mechanical properties of the material. In this study, material low carbon steel ST 41 will be tested using a hardness testing (hardness test). It aims to find out how much the violence that can be seen from the difference in the thickness of the galvanized coating on the material that is known to influence the value of the material hardness ketebelan different galvanized coating. Keywords: Hot Dipped Galvanizing, Hardness Test, ST 41


Detil Peneliti

Dosen Pembimbing 1 :Muhammad Muhadi Eko Prayitno
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK PERMESINAN KAPAL
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.