Analisa Cacat Hasil Pengelasan Bottom Slope Tube Dengan Uji Radiografi

WELDING DEFECT ANALYSIS OF BOTTOM SLOPE TUBE WITH RADIOGRAPHY TEST

Prenika Ayu Anggraini (6311030030)


Abstrak

ANALISA CACAT HASIL PENGELASAN BOTTOM SLOPE TUBE DENGAN UJI RADIOGRAFI Nama Mahasiswa : Prenika Ayu Anggraini NRP : 6311030030 Jurusan : Teknik Permesinan Kapal ,PPNS Dosen Pembimbing : Wahyudi, ST, MT. ABSTRAK Boiler merupakan komponen utama penghasil uap pada PLTU PT.YTL Jawa Timur, bottom slope tube merupakan komponen pendukung penghasil steam pada boiler. Bottom slope tube terletak pada posisi yang kritis, karena bottom slope tube terletak di bagian dasar boiler, flay ash dan slag dari komponen bagian atas boiler seperti: superheater tube dan economizer tube yang jatuh ke bawah dapat mempengaruhi struktur material pipa berubah, perubahan tersebut juga berpengaruh pada kekuatan las sehingga bisa terjadi kebocoran. Sehingga dilakukan pengujian NDT pada pipa-pipa bottom slope yang terdapat pada Pembangkit Listrik Tenaga Uap (PLTU) PT. Yeoh Tiong Lay (YTL) Jawa Timur unit 6. Metode uji yang dilakukan adalah uji radiografi, hasil pengujian tersebut digunakan untuk mengetahui cacat las yang terjadi pada permukaan maupun di dalam las yang terdapat dalam bottom slope tube menggunakan standar ASME 1 dan ASME V section 2 tentang standart penerimaan cacat dan pemilihan teknik penyinaran untuk boiler dan pressure vessel . Hasil dari pengujian radiografi akan nampak pada film yang selanjutnya akan di analisa untuk mengetahui jenis cacat yang terjadi. Dari hasil analisa menunjukkan bahwa indikasi cacat porosity pada bottom slope tube tidak boleh melebihi 3,18 mm, pada join 2 no 70 south terindikasi cacat porosity dengan diameter 2mm tidak melebihi batas ketentuan sehingga tidak perlu dilakukan repair, dan pada join no 119A north terindikasi cacat porosity dengan diameter 4 mm perlu dilakukan repair. Kata kunci : bottom slope tube, radiografi, jenis cacat


Abstract

WELDING DEFECT ANALYSIS OF BOTTOM SLOPE TUBE WITH RADYOGRAPHY TEST Name : Prenika Ayu Anggraini NRP : 6311030030 Jurusan : Marine Engineering ,PPNS Counsellor lecturer : Wahyudi, ST, MT. ABSTRACT Boiler is a major component in producing steam power plant in East Java PT.YTL bottom slope is supporting components producer tube steam boiler. Bottom slope tube lies in a critical position, because the bottom slope is located at the bottom of the tube boilers, flay ash and slag from the top of the boiler components such as superheater tubes and economizer tubes falling down can affect the structure of the pipe material change, such changes also affect the weld strength so that it can leak. So do the NDT testing pipes bottom slope contained in steam power plant (power plant) PT. Yeoh Tiong Lay (YTL) East Java unit 6. Methods of tests performed was radiography test, the test results are used to determine the weld defect that occurs on the surface and inside weld contained in the tube using a bottom slope of 1 and ASME standard ASME standard V acceptance of disability and the selection of radiation technique for boiler and pressure vessel. The results of the test will appear on the radiographic film will then be analyzed to determine the types of defects that occur. From the results of the analysis show that the indication of porosity defects in the tube bottom slope should not exceed 3.18 mm, the joint 2 No. 70 south indicated porosity defects with a diameter of 2mm does not exceed the specified limits so no need for repair, and to join 119a north indicated no defects porosity with a diameter of 4 mm is necessary to repair. Keywords: bottom slope tube, radiography, type of defect.


Detil Peneliti

Dosen Pembimbing 1 :Wahyudi
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK PERMESINAN KAPAL
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.