ANALISA CACAT HASIL PENGELASAN PIPA 6 INCH SCH. 80 CARBON STEEL MENGGUNAKAN METODE RADIOGRAFI TEST (RT)

DEFECT ANALYSIS OF 6 INCH SCH. 80 CARBON STEEL PIPE WELDING WITH RADIOGRAPHY TEST METHOD (RT)

Dandy Kurniawan Putra (6311030009)


Abstrak

ABSTRAK Dalam sambungan pipa harus memiliki struktur konstruksi yang kuat dan terutama sambungan las nya (welding). Pada sektor HRSG(Heat Recovery Steam Generator) menggunakan pipa 6 inch sch. 80 carbon steel dengan tipe sambungan las Butt Joint. Ketidak sempurnaan dalam proses pengelasan ataupun terdapat cacat pada sambungan las pipa akan mempengaruhi keselamatan dan keamanan di area tersebut. Untuk mengetahui cacat yang timbul, maka perlu dilakukan pengujian NDT menggunakan radiografi test. Pengujian radiografi test merupakan pengujian Non Destructive Test(NDT). Proses pengujian radiografi test harus sesuai prosedur yang telah ditentukan, pengujian radiografi test menggunakan standar dari ASME section IX. Sesuai standar yang telah ditentukan, sebelum pengujian maka harus dilakukan kalibrasi alat sampai dengan proses scaning. Hal ini dilakukan bertujuan untuk mendukung kesempurnaan dalam proses pengujian NDT. Cacat yang timbul pada hasil lasan pipa 6 inch carbon steel masuk kategori kelas dari ASME section IX yang akan menentukan repair atau tidaknya sambungan las tersebut. Dari hasil analisa menunjukan sambungan las pipa 6 inch carbon steel terdapat cacat yang melebihi toleransi yang ditentukan. Hasil evaluasi menunjukan cacat lasan yang berada pada film 7-14 dimana sesuai standar penerimaan menurut ASME section IX termasuk dalam kategori cacat porosity. Kata Kunci : Carbon Steel, Non Destructive Test, ASME section IX


Abstract

ABSTRACT In connection pipe must have a strong construction structure and especially its welded joints (welding). In the sector of the HRSG (Heat Recovery Steam Generator) using 6-inch pipe sch. 80 carbon steel butt weld joint type. Imperfections in the welding process or there are defects in the weld joint pipe will affect the safety and security in the area. To find defects that arise, it is necessary to NDT testing using radiographic tests. Radiographic Testing test is a test of the Non Destructive Test (NDT). Radiographic testing process should be appropriate test procedures have been specified, radiographic testing using a standard test of ASME section IX. As per the prescribed standards, testing should be performed before calibration tool until the scanning process. This is done aims to support excellence in NDT testing process. Defects that arise on the results of weld carbon steel pipe 6 inches in the category of ASME section IX class that will determine whether or not to repair the weld joint. From the analysis shows the weld carbon steel pipe 6 inches there are defects which exceed the specified tolerances. The evaluation results showed that weld defects are the films where segmen 7-14 admission standards according to ASME section IX included in the category of porosity defects. Keywords: Carbon Steel, Non Destructive Test, ASME section IX


Detil Peneliti

Dosen Pembimbing 1 :Wahyudi
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK PERMESINAN KAPAL
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.