ANALISA PENGARUH BUTTERING TERHADAP KEKERASAN MATERIAL A 283

ANALYSIS THE EFFECT OF BUTTERING ON MATERIAL A 283

Muhammad Zacky Alami (6310030031)


Abstrak

ANALISA PENGARUH BUTTERING TERHADAP KEKERASAN MATERIAL A 283 Nama Mahasiswa : Muhammad Zacky Alami NRP. 6310030031 Nama Dosen Pembimbing : Bambang Antoko, ST., MT NIP. 196310261988031001 ABSTRAK Dalam proses pembuatan tube side, terkadang terdapat kesalahan pada saat proses drilling. Oleh karena itu perlu adanya repair pada material yang mengalami kesalahan tersebut. Salah satunya adalah dengan cara buttering. Buttering adalah teknik pengelasan di mana dilakukan penambalan dalam rangka untuk mencapai sifat yang diinginkan atau dimensi yang diperlukan. Dalam hal ini material yang digunakan adalah A 283. Akan tetapi material A 283 yang mengalami buttering akan mengalami penurunan kualitas. Sehingga kualitas dari material A 283 tidak lagi seperti awal. Dalam penelitian ini digunakan empat variasi untuk membandingkan nilai kekerasan pada tiap variasi. Penelitian ini dilakukan dengan teknik buttering untuk material A 283 dengan sudut cacat 60o, 75o, 90o dan non-buttering untuk material tanpa cacat sehingga dapat diketahui bagaimana pengaruh buttering terhadap tingkat kekerasan rata-rata pada masing-masing variasi tersebut. Untuk mengetahui pengaruh buttering terhadap tingkat kekerasan material A 283 perlu diadakan uji hardness, di mana uji hardness yang dilakukan adalah dengan menggunakan metode Vickers. Dari penelitian pada masing-masing variasi didapatkan hasil bahwa material yang tidak mengalami buttering mempunyai nilai kekerasan yang paling rendah yaitu sebesar 129,608 HVN. Sedangkan material dengan sudut cacat 90o mempunyai nilai kekerasan yang paling besar yaitu sebesar 201,295 HVN. Kata Kunci: Buttering, A 283, Uji Kekerasan, Nilai Kekerasan


Abstract

ANALYSIS THE EFFECT OF BUTTERING ON MATERIAL A 283 Name : Muhammad Zacky Alami NRP. 6310030031 Adviser : Bambang Antoko, ST., MT NIP. 196310261988031001 ABSTRACT In the process of making the tube side, sometimes there are errors during the process of drilling. Therefore, it is necessary to repair the material that had the error. One of them is by way of buttering. Buttering is a welding technique in which the filling is done in order to achieve the desired properties or dimensions are required. In this case the material used is A 283. But material A 283 which had buttering will decrease the quality. So the quality of the material is no longer like the beginning. This research used four variations to compare the hardness value for each variations. This research was conducted by buttering technique for material A 283 with the defect angle 60o, 75o, 90o, and material non-buttering for material without defect so that it can be seen how the effect of the buttering the average level for hardness on each of these variations. To determine the effect of the buttering material hardness A 283 should be a hardness test, where the hardness test is carried out by using the Vickers method. Of research on each of the variations showed that the material does not undergo buttering have the lowest hardness value that equal to 129,608 HVN. While the material at defect angle 90o have the biggest hardness value that is equal to 201,295 HVN. Key Words: Buttering, A 283, Hardness Test, Hardness Value


Detil Peneliti

Dosen Pembimbing 1 :Bambang Antoko
Dosen Pembimbing 2 : Bambang Antoko

Program Studi : D3 - TEKNIK PERMESINAN KAPAL
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.