PENGARUH PREHEAT TERHADAP NILAI KEKERASAN PADA MATERIAL KI-GRADE A

PREHEAT EFFECT ON MATERIAL HARDNESS AT KI GRADE-A

Ryan Agung Kurniyawan C. P. (6213030026)


Abstrak

ABSTRAK PENGARUH PREHEAT TERHADAP NILAI KEKERASAN PADA MATERIAL KI GRADE - A Oleh: Ryan Agung Kurniyawan C.P. NRP: 6213030026 Kapal merupakan kendaraan pengangkut penumpang dan barang dilaut. Dalam pembangunan sebuah kapal terdapat hal yang perlu di perhatikan yaitu proses pengelasan pada lambung kapal. Salah satu proses pengelasan yang di kenal dalam pembangunan kapal yaitu proses pengelasan SMAW. Dalam pengelasan SMAW parameter-parameter yang harus diperhatikan adalah kuat arus,tegangan,kecepatan pengelasan,dan heatinput. Adanya parameter-parameter tersebut berpengaruh terhadap luasan HAZ.Selain adanya parameter-parameter dalam pengelasan, terdapat juga metode-metode pengelasan yang dapat menunjang agar mendapatkan hasil pengelasan yang baik. Dari hal tersebut dilakukan penelitian dengan membandingkan nilai kekerasan pada material setelah pengelasan dengan perlakuan preheat dan tanpa preheat. pengelasan sesuai dengan kondisi di lapangan, dimana sebelum pengelasan SMAW tanpa di beri perlakuan preheat dan di beri perlakuan preheat.Kemudian dilakukan pengujian Macro Etcha, dan Uji hardness. Untuk membuktikan pengaruh preheat terhadap nilai kekerasan pada matrial tersebut. Dari hasil pengujian Macro Etcha dan Uji hardness ternyata dapat membuktikan bahwa semakin besar preheat maka matrial tersebut semakin keras.Dan temperature preheat maksimal yaitu 250? C, di lihat dari hasil pengujian Macro Etcha, luasan HAZ menjadi lebih besar karena pengaruh dari preheat. Dan di lihat dari hasil pengujian Uji hardness kekerasan plat naik karena pengaruh preheat. Katakunci: PengelasanSMAW, HAZ, Preheat, Macro Etcha, Uji Hardness,


Abstract

ABSTRACT PREHEAT EFFECT ON MATERIAL HARDNESS AT KI GRADE-A By: Ryan Agung Kurniyawan C.P. NRP: 6213030026 Ship is a vehicle transporting passengers and goods at sea. In the construction of a ship there are things that need to be noticed that the process of welding the hull. One of the welding process known in the construction of ships which SMAW welding process. In SMAW welding parameters that should be considered is a strong current, voltage, welding speed, and heatinput. The existence of these parameters affect the extent of their HAZ.Selain in welding parameters, there are also methods of welding that can support in order to obtain good welding results. From this research is done by comparing the value of the material hardness after welding preheat treatment with and without preheat. welding in accordance with conditions on the ground, where before SMAW welding without preheat treatment given and given treatment preheat.Kemudian testing Etcha Macro and hardness test. To prove the effect of preheat to the value of hardness in the matrial. From the test results Etcha Macro and hardness test was found to prove that the greater preheat the matrial is increasingly keras.Dan maximum preheat temperature of 250 ? C, in view of the test results Macro Etcha, HAZ area becomes larger because of the influence of preheat. And in view of the hardness test hardness test results rose because of the influence of preheat plate Keywords: Welding SMAW, HAZ, Preheat, Macro Etcha, Hardness Test, Acceptance Criteria


Detil Peneliti

Dosen Pembimbing 1 :Gaguk Suhardjito
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK BANGUNAN KAPAL
Angkatan : 2013


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.