PENGARUH VARIASI KUAT ARUS PENGELASAN FCAW DAN SAW TERHADAP SIFAT MEKANIK PLAT LAMBUNG KAPAL TERNAK 1200 GT

THE EFFECT OF VARIATIONS IN CURRENT CAPACITY WITH FCAW AND SAW WELDING TO MECHANICAL PROPERTIES OF PLATE ON LIVESTOCK SHIP 1200 GT

Ulumuddin Fatwa Wahid (6213030025)


Abstrak

ABSTRAK PENGARUH VARIASI KUAT ARUS PENGELASAN FCAW DAN SAW TERHADAP SIFAT MEKANIK PADA PLAT LAMBUNG KAPAL TERNAK 1200 GT Oleh: Ulumuddin Fatwa Wahid NRP: 6213030025 Sebagian besar pengelasan pada plat lambung kapal ternak 1200 GT menggunakan kombinasi pengelasan FCAW dan SAW. Sedangkan, belum ada WPS yang mengatur tentang las kombinasi tersebut. Hal tersebut berakibat pada banyak ditemukan perbedaan variasi kuat arus yang digunakan oleh sub-kontraktor yang sedang menyelesaikan pembangunan kapal tersebut. Sehingga dikhawatirkan dari variasi tersebut ada pengelasan yang tidak memenuhi Acceptance Criteria dilihat dari sifat mekaniknya. Dari hal tersebut dilakukan penelitian dengan mengambil sample kuat arus rendah, sedang dan tinggi sesuai yang terjadi di lapangan. Pengelasan dilakkan sejumlah 3 layer yaitu Root dan Isi menggunakan proses las FCAW, serta Caping menggunakan proses las SAW. kemudian dilakukan pengujian Macro Etcha, Uji Tarik, dan Uji Bending. Untuk membuktikan variasi kuat arus tersebut apakah berpengaruh pada lebar HAZ, nilai Yield Strength, nilai Ultimate Strength, elongation dan hasil uji bending. Dari hasil pengujian Macro Etcha, Uji Tarik dan Uji Bending ternyata dapat membuktikan pengaruh variasi kuat arus dengan pengelasan FCAW dan SAW terhadap sifat mekanik. Hasil pengujian Macro Etcha dapat membuktikan semakin tinggi kuat arus maka lebar HAZ semakin tinggi. Hasil Pengujian Tensile Test kuat arus rendahmemiliki nilai Ultimate Strength tertinggi, dan kuat arus sedang memiliki nilai Yield Strengh dan Elongation tertinggi. Dan hasil Pengujian Bending spesimen dengan kuat arus rendah dan sedang memiliki hasil uji bending yang bagus baik itu pengujian pada Face bend dan Root bend, sedangkan pada kuat arus tinggi terdapat cacat yang ditemukan pada hasil pengujian Root Bend. Kata kunci : Pengelasan FCAW, Pengelasan SAW, HAZ, Yield Stength, Ultimate Strength, Elongation, Macro Etcha, Tensile, Bending, Acceptance Criteria


Abstract

ABSTRACT THE EFFECT OF VARIATIONS IN CURRENT CAPACITY WITH FCAW AND SAW WELDING TO MECHANICAL PROPERTIES OF PLATE ON LIVESTOCK SHIP 1200 GT By: Ulumuddin Fatwa Wahid NRP: 6213030025 Most of the welding on the hull plate livestock 1200 GT uses a combination of welding FCAW and SAW . Meanwhile , there has been no WPS welding regulating such combinations. This resulted in many variations differences were found for the current strength used by sub - contractors who are completing the construction of the ship. So feared of such variations exist welding does not meet the Acceptance Criteria views from its mechanical properties . From this research is done by taking a sample current of low, medium and high according happens on the field . Welding use number of 3 layers namely Root and Content using FCAW welding process , as well as Caping using SAW welding processes . Then use Macro Etcha testing , Tensile Test , and BendingTest . To prove the current strong variation does affect the width of HAZ , the value of Yield Strength , Ultimate Strength value , elongation and bending test results . From the test results of Macro Etcha , Bending Test, Tensile Test and was found to prove the effect of variations in the current strength with FCAW and SAW welding on mechanical properties . The result of Macro Etcha test could prove stronger the higher the current , the higher HAZ width . The result of Tensile Testthe low of current have the Ultimate Strengthi highest value , and strong currents are having a value Yield strengh and high elongation . And the result of Bending Test specimens with low and medium strong currents have great bending test results of both tests on Face Root bend and bend, whereas at high currents are strong defects found on the test results Root Bend . Keywords : FCAWWelding , SAW Welding , HAZ , Yield stength , Ultimate Strength , elongation , Macro Etcha , Tensile , Bending , Acceptance Criteria.


Detil Peneliti

Dosen Pembimbing 1 :Rachmad Tri Soelistijono
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK BANGUNAN KAPAL
Angkatan : 2013


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.