Pengaruh TIG Dressing terhadap lebar HAZ pada proses pengelasan SMAW

TIG DRESSING EFFECT OF WIDE HAZ WITH SMAW WELDING PROCESS

Rizky Puji Arditama (6213030024)


Abstrak

ABSTRAK PENGARUH TIG DRESSING TERHADAP LEBAR HAZ PADA PROSES PENGELASAN SMAW Oleh: Rizky Puji Arditama NRP: 6213030024 Kapal merupakan kendaraan pengangkut penumpang dan barang dilaut. Dalam pembangunan sebuah kapal terdapat hal yang perlu di perhatikan yaitu proses pengelasan pada lambung kapal. Salah satu proses pengelasan yang di kenal dalam pembangunan kapal yaitu proses pengelasan SMAW. Dalam pengelasan SMAW parameter-parameter yang harus diperhatikan adalah kuat arus, tegangan, kecepatan pengelasan, dan heat input. Adanya parameter-parameter tersebut berpengaruh terhadap luasan HAZ. Selain adanya parameter-parameter dalam pengelasan, terdapat juga metode-metode pengelasan yang dapat menunjang agar mendapatkan hasil pengelasan yang baik. Dari hal tersebut dilakukan penelitian dengan mengambil salah satu metode yaitu TIG-Dressing. Dengan melakukan pengelasan sesuai dengan kondisi di lapangan, dimana pengelasan SMAW tanpa di beri perlakuan TIG-Dressing dan di beri perlakuan TIG-Dressing. Kemudian dilakukan pengujian Macro Etcha, dan Uji Tarik. Untuk membuktikan pengaruh TIG-Dressing tersebut apakah masih sesuai dengan acceptance Criteria yang ada. Dari hasil pengujian Macro Etcha dan Uji Tarik ternyata dapat membuktikan bahwa pengaruh TIG-Dressing masih memenuhi standart Acceptance Criteria. Karena tidak terdapat cacat dan nilai kekuatan tarik masih memenuhi standar. Namun di lihat dari hasil pengujian Macro Etcha, luasan HAZ menjadi lebih besar karena pengaruh dari TIG-Dressing. Dan di lihat dari hasil pengujian Uji Tarik kekuatan tarik menurun karena pengaruh TIG-Dressing. Kata kunci : Pengelasan SMAW, HAZ, TIG-Dressing, Macro Etcha, Uji Tarik, Acceptance Criteria


Abstract

ABSTRACT TIG DRESSING EFFECT OF WIDE HAZ WITH SMAW WELDING PROCESS By: Rizky Puji Arditama NRP: 6213030024 Ship is a vehicle transporting passengers and goods at sea. In the construction of a ship there are things that need to be noticed that the process of welding the hull. One of the welding process known in the construction of ships which SMAW welding process. In SMAW welding parameters that should be considered is a strong current, voltage, welding speed, and heat input. The existence of these parameters affect the HAZ area. In addition to the parameters in welding, there are also methods of welding that can support in order to obtain good welding results. From this research is done by taking one of the methods that is TIG-Dressing. By doing welding in accordance with conditions on the ground, where the SMAW welding without given treatment TIG-Dressing and given treatment TIG-Dressing. Then testing Etcha Macro, and Tensile Test. To prove the effect of TIG-dressing is still in accordance with the existing Criteria acceptance. From the test results Tensile Test Macro Etcha and was able to prove that the effect of TIG-Dressing still meet the standards Acceptance Criteria. Because there are no defects and tensile strength values still meet the standards. However, in view of the test results Macro Etcha, HAZ area becomes larger because of the influence of TIG-Dressing. And in view of the test results Tensile Test tensile strength decreased because of TIG-Dressing. Keywords: Welding SMAW, HAZ, TIG-Dressing, Macro Etcha, Tensile Test, Acceptance Criteria


Detil Peneliti

Dosen Pembimbing 1 :Heru Lumaksono
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK BANGUNAN KAPAL
Angkatan : 2013


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.