PENGARUH VARIASI KUAT ARUS PADA PENGELASAN GMAW MATERIAL ALUMUNIUM 5083 TERHADAP MECHANICAL PROPERTIES

EFFECT OF VARIATION IN STRONG FLOW GMAW WELDING MATERIAL MECHANICAL PROPERTIES OF ALUMINUM 5083

Ivals Dhean Airlangga (6213030017)


Abstrak

ABSTRAK PENGARUH VARIASI KUAT ARUS PADA PENGELASAN GMAW MATERIAL ALUMUNIUM 5083 TERHADAP MECHANICAL PROPERTIES Oleh: Ivals Dhean Airlanga NRP: 6213030017 Aluminium merupakan logam yang ringan namun kuat dan tahan terhadap karat.Hal inilah yang membuat logam ini cocok untuk dikembangkan dalam bidang perkapalan.Salah satu jenis aluminium yang sering dipergunakan dalam pembuatan kapal adalah aluminium 5083 seperti pada bangunan atas kapal (Jet Foil) dan tangga di KRI.RE Martadinata 1.Kualitas hasil pengelasan merupakan salah satu faktor utama yang menentukan kekuatan suatu struktur termasuk bangunan kapal dan kekuatan sambungan kontruksi. Pada penelitian ini digunakan tiga variasi kuat arus (ampere) pada pengelasan GMAW.Dengan melakukan pengelasan sesuai pada kondisi di lapangan, dan Parameter pengelasan yang digunakan yaitu kuat arus 110A, 132A, 156A.dimana untuk mengetahui dampak terhadap variasi kuat arus pada pengelasan aluminium 5083 terhadap kekuatan mekanik dan makro, maka di lakukan pengujian Tarik dan Uji Macro Etcha. Berdasarkan hasil penelitian pengujian Macro Etcha di dapatkan hasil fusi yang baik pada specimen A3 dengan 156 A, namun daerah HAZ juga semakin lebar.sedangkanhasil tidak fusidan terdapat cacat porosity terdapat pada amper 110 A dan 132A dengan daerah HAZ kecil. sedangkan untuk hasil pengujian tarik 156 A mendapatkan hasil pengujian tarik dengan nilai tertinggi yaitu sebesar 235,215 Mpa dan pada 110 A mendapatkan hasil pengujian tarik dengan nilai terendah yaitu sebesar 125,605 Mpa. Kata kunci: Alumunium 5083, GMAW, Uji Tarik, Uji Macro Etcha.


Abstract

ABSTRACT EFFECT OF VARIATION IN STRONG FLOW GMAW WELDING MATERIAL MECHANICAL PROPERTIES OF ALUMINUM 5083 By: Ivals Dhean Airlangga NRP: 6213030017 Aluminum is a metal that is lightweight yet strong and resistant to rust. This is what makes this metal is suitable to be developed in the field of shipping. One type of aluminum is often used in shipbuilding is aluminum 5083 as the buildings on the boat (Jet Foil) and stairs in KRI.RE Martadinata 1. The quality of the welding is one of the main factors that determine the strength of a structure including ship building and connection strength construction. In this study used three variations of the electric current (amperes) GMAW welding. By doing welding according to the conditions in the field, and the welding parameters used are strong currents 110A, 132A, 156a. where to find out the impact on the variation of the current strength 5083 aluminum welding to mechanical forces and macro, then do a test Pull and Test Macro Etcha. Based on the results of testing at the Etcha Macro fusion get good results on the specimens A3 to 156 A, but also the wider region HAZ. while the results are not there are defects of fusion and porosity contained in Ampere 110 A and 132 A with a small HAZ area. while for the results of tensile testing 156 A gain tensile test results with the highest value in the amount of 235.215 MPa and at 110 A gain tensile test results with the lowest value that is equal to 125.605 Mpa. Keywords: Aluminum 5083, GMAW, Tensile Test, Test Macro Etcha


Detil Peneliti

Dosen Pembimbing 1 :Rachmad Tri Soelistijono
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK BANGUNAN KAPAL
Angkatan : 2013


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.