Analisa sifat mekanis pengelasan GMAW (Gas Metal Arc Welding), FCAW (Flux Cored Arc Welding) dengan metode uji tensile dan bending

ANALYSIS OF THE WELDING MECHANICAL PROPERTIES OF GMAW (GAS METAL ARC WELDING), FCAW (FLUX CORED ARC WELDING) AND TEST METHOD BENDING AND TENSILE TEST

M. Bayu Rizqi Priyanto (6212030020)


Abstrak

Mutu dari hasil pengelasan di samping tergantung dari pengerjaan lasnya sendiri dan juga sangat tergantung dari persiapan sebelum pelaksanaan pengelasan, karena pengelasan adalah proses penyambungan antara dua bagian logam atau lebih dengan menggunakan energi panas. Pada penelitian ini pengelasan yang digunakan antara lain GMAW (Gas Metal Arc Welding), FCAW (Flux Cored Arc Welding) Hal ini sangat erat hubungannya dengan arus listrik, ketangguhan, cacat las, serta retak yang pada umumnya mempunyai pengaruh yang fatal terhadap keamanan dari konstruksi yang dilas. Penelitian ini bertujuan untuk mengetahui sifat mekanis hasil pengelasan dari GMAW dan FCAW dengan posisi 1G dan polarity DC ( ). Material yang di gunakan adalah baja karbon rendah A36 dengan tebal masing-masing 10 mm. Test yang dilakukan adalah dengan pengujian merusak (Destructive Test/DT) dengan metode tensile test dan bending test. Hasil tensile test menunjukkan nilai rata-rata kekuatan tarik yang paling tinggi pada proses pengelasan FCAW dengan nilai 425,31 Mpa sedangkan pada proses pengelasan GMAW nilai rata-rata sebesar 414,18 Mpa, dan pada pengujian letak patahan semua spesimen uji pada daerah base metal, sedangkan pada pengujian bending proses pengelasan GMAW dan FCAW pada face bend tidak terdapat cacat, sedangkan pada root bend terdapat cacat hanya pada proses pengelasan GMAW sebesar 1,9 mm dan 1,8 mm dan proses pengelasan FCAW tidak terdapat cacat. Dari hasil test uji di atas proses pengelasan GMAW dan FCAW dikatakan berhasil karena masih dalam acceptance criteria masing-masing pengujian. Hanya saja pada proses pengelasan FCAW yang hasilnya lebih baik. Kata Kunci : A36 , Pengelasan GMAW


Abstract

The quality result of the welding in addition to depending on the welding his own and also depends on the preparations before the implementation of the welding, because the welding is the process of switching between two pieces of mteal or more with the use of heat energy. In this study welding process that in use GMAW (Gas Metal Arc Welding), FCAW (Flux Cored Arc Welding) it is very closely to do with the follow of electricity, toughness, defect, as well as cracks in general have leverage that is fatal to the safety of construction that is. This study aims to know the nature of the mechanical of welding GMAW and FCAW and the position of welding process with 1G and polarity DC ( ). The material in use a low carbon steel A36 with thickness 10 mm. Test is carried out with the Destructive Test (DT) with the method of tensile test and bending test. The tensile test showed the average value of the tensile strength the most high in the process of welding FCAW with the value of 425,31 Mpa, while in the process of welding GMAW the value of an average of 414,18 Mpa, and on testing is the fault all specimen tests on the base metal, while in bending test the process of welding GMAW and FCAW in the face bend there is not defect, while at the root bend there are defect only in the process of welding GMAW with size of defect 1,9 and 1,8 mm and the process of welding FCAW there is no defects. From the speciment test, the welding process of GMAW and FCAW be succesful because is still in acceptance criteria of each test. Only on the FCAW welding process that results are better. The Keywords: A36, Welding GMAW


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK BANGUNAN KAPAL
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.