ANALISA KEKUATAN PENGELASAN GMAW ( GAS METAL ARC WELDING ), FCAW ( FLUX CORED ARC WELDING ) DENGAN METODE UJI IMPACT DAN NILAI EKONOMIS

ANALYSIS OF THE WELDING STRENGTH OF GMAW (GAS METAL ARC WELDING), FCAW (FLUX CORED ARC WELDING) AND TEST METHOD OF IMPACT AND ECONOMIC VALUE

Guster Irvan Ginting (6212030012)


Abstrak

ABSTRAK Dalam era sekarang ini, perkembangan teknologi pengelasan sangat cepat, terutama dalam pembangunan kapal baru dan memperbaiki konstruksi kapal. Pekerjaan pengelasan sering kali mengalami keterlambatan, hal ini yang menyebabkan kehilangan biaya, waktu dan bahan material yang telah dipakai. Mengembangkan kecepatan dan efisiensi pekerjaan pengelasan harus memilih metode pengelasan yang sesuai. Penelitian ini akan menjelaskan perbedaan dari dua metode pengelasan terdiri dari FCAW dan GMAW, terhadap nilai kekuatan dan nilai ekonomi. Kekuatan hasil pengelasan diuji dengan uji rusak (Dectructive test) yaitu uji Impact, dan nilai ekonomis yang akan ditinjau dari perhitungan kecepatan las dan biaya elektroda yang dikonsumsi untuk mengetahui perbedaan nilai ekonomi pada setiap metode pengelasan. Hasil pengujian impact pada suhu 24,8 0C menunjukkan bahwa metode pengelasan FCAW lebih besar 3,3% dibandingkan metode pengelasan GMAW. Sedangkan hasil pengujian impact pada suhu 6,5 0C menunjukkan bahwa metode pengelasan FCAW lebih besar 23% dibandingkan metode pengelasan GMAW. Pengelasan dengan metode FCAW lebih ekonomis 8,5% dibandingkan dengan metode pengelasan GMAW. Metode pengelasan GMAW memiliki kecepatan 19% lebih cepat dibandingkan dengan metode pengelasan FCAW. Kata kunci : FCAW, GMAW, Impact Test, Nilai Ekonomis


Abstract

ABSTRACT In this era, development of technology of welding is very fast, especially in the development of new ship construction and repair of ships. Welding work often experience a delay, and it is that is causing the loss of cost, time and materials that have been used. Developing the speed and efficiency of welding work must choose kind of the appropriate welding method. This research will explain the difference of the two methods of welding FCAW and GMAW consists of, against the value of strength and economic value. The strength of the weld is tested with defective test (Dectructive test) is a test of the Impact, and economic value which will be reviewed in the calculation of the speed of the welding electrode is consumed and the cost for knowing the difference of economic value at each welding methods. The results of the impact test at a temperature of 24, 8 0C shows that the method of welding FCAW larger 3.3% compared to GMAW welding methods. While the results of the impact test at a temperature of 6, 5 0C showed that welding method FCAW 23% greater than the GMAW welding method. FCAW welding with a more economical method of 8,5% compared with GMAW welding method. GMAW welding method has a speed of 19% faster than with a FCAW welding methods. keywords : FCAW, GMAW, Impact Test, Economic Value


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK BANGUNAN KAPAL
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.