PENGARUH PARAMETER PENGELASAN SPOT WELDING TERHADAP SHEAR STRENGTH DAN DIAMETER NUGGET PADA MATERIAL SUS 304 DAN SS 400

EFFECT OF SPOT WELDING PARAMETERS AGAINST SHEAR STRENGTH AND NUGGET DIAMETER OF SUS 304 AND SS 400

Sultan Yudhistira (6211030019)


Abstrak

Penelitian ini bertujuan untuk mengetahui pengaruh parameter pengelasan yaitu arus dan waktu pengelasan terhadap diameter nugget dan kekuatan geser dari sambungan dua material berbeda menggunakan las resistansi listrik. Material yang digunakan adalah baja karbon rendah SS 400 dan stainless steel dengan tebal masing-masing 2 mm. Pengelasan dilakukan dengan variasi arus 10-14 kA dan waktu 22-28 cycle. Test yang dilakukan adalah test uji geser dan makro etsa. Hasil test uji geser menunjukkan rata-rata kekuatan geser yang paling tinggi adalah 2899,69 Kgf dengan arus 14 kA dan waktu pengelasan 28 cycle sedangkan yang paling rendah adalah 2423,48 Kgf dengan arus 10 kA dan waktu pengelasan 22 cycle. Hasil pengamatan diameter nugget melalui test makro etsa menunjukkan nilai diameter nugget yang paling tinggi adalah 10,6 mm dengan arus 14 kA dan waktu pengelasan 28 cycle sedangkan yang paling rendah adalah 6,58 mm dengan arus 10 kA dan waktu pengelasan 22 cycle. Dari hasil test uji geser diatas diketahui bahwa semakin tinggi arus dan waktu pengelasan, maka semakin tinggi pula nilai kekuatan gesernya, kecuali penyimpangan yang terjadi pada parameter dengan arus 12 kA dengan waktu 28 cycle. Sedangkan dari test makro etsa dapat diketahui semakin tinggi arus dan waktu pengelasan, maka semakin tinggi pula diameter nugget yang dihasilkan.


Abstract

This study aims to determine the effect of welding parameters, namely welding current and time against nugget diameter and the shear strength of the welded connection of two different materials using resistance spot welding. The material used is low carbon steel SS 400 and stainless steel SUS 304 each with a thickness of 2 mm. Welding peformed with 10-14 kA current and weld time 22-28 cycle variations. Test carried out by tensile-shear testing machine and macro-etching. Shear test result showed the average highest shear strength was 2899,69 Kgf with current of 14 kA and welding time of 28 cycle while the lowest was 2423.48 Kgf with a current of 10 kA and welding time of 22 cycles. Nugget diameter observations through macro-etching test indicate that the value of the nugget diameter of 10.6 mm is highest with a current 14 kA and welding time of 28 cycles while the lowest was 6.58 mm with a current of 10 kA and welding time of 22 cycles. From the results of the shear test, it is known that the higher the welding current and time, the higher the shear strength values, except for parameter deviations occur in the current 12 kA with a time of 28 cycles. While from the macro-etching test can be seen the higher current and welding time, the higher the nugget diameter were produced.


Detil Peneliti

Dosen Pembimbing 1 :Zuhri Noor
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK BANGUNAN KAPAL
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.