PENGARUH VARIASI INTERVAL WAKTU TERHADAP KEKUATAN LAPISAN PENGECATAN

THE EFFECT OF TIME INTERVAL VARIATION TO ADHESIVE OF COATING

Dwiky Syamcahyadi Rahman (6210030003)


Abstrak

Pelat yang sudah di blasting mempunyai batasan waktu untuk diaplikasi pengecatan. Menurut pengalaman interval waktu tersebut tidak boleh lebih dari 4 jam. Tetapi fakta dilapangan interval waktu antara setelah blasting sampai dengan pengecatan melebihi dari ketentuan tersebut. Padahal interval waktu tersebut sangat berpengaruh pada hasil pengecatan. Untuk mengetahui hasil pengecatan baik atau tidak, salah satu cara yang dilakukan yaitu uji kekuatan atau pull off test. Dengan melihat permasalahan tersebut, maka melalui penelitian ini ingin diketahui pengaruh variasi interval waktu terhadap kekuatan lapisan pengecatan dengan melakukan pengujian kekuatan atau pull off test. Telah dilakukan penelitian pada material baja dengan ukuran 300 mm x 300 mm x 10 mm sebanyak 6 test piece yang diblasting dan di ukur surface roughness, kebersihan, relative humidty, temperature permukaan dan dew point. Material uji dicat dengan variasi interval 1 jam, 3 jam dan 5 jam. Dari hasil pengecatan, diukur ketebalan cat kering (DFT) dan di uji kekuatan lapisan pengecatan. Setelah itu dilakukan analisa pengaruh variasi interval waktu terhadap kekuatan lapisan pengecatan. Dari analisa didapatkan kesimpulan bahwa semakin lama interval waktu semakin menurun kekuatan lapisan pengecatan. Tetapi kekuatan lapisan pengecatan pada interval waktu 1 jam, 3 jam dan 5 jam dapat diterima karena melebihi ketentuan standard ISO 16276-1 yaitu 3 MPa. Untuk interval waktu maksimum pada relative humidity 70-80% yang dihitung dengan persamaan garis lurus y = -0.70875x 7.52375 didapatkan interval waktu maksimum yaitu 6 jam 24 menit.


Abstract

Plate that is blasted in have time limit to be painted. According to the experience, the time interval may not be longer than 4 hours. But the fact , interval between after blasting to painting is longer than it. Though, the time interval is very influential to the result of the painting. to determine results of the painting, one of the ways that is done is adhesion test or pull off test. By looking at these problems, so with this research want to be known effect of the time interval variation to adhesive of coating with adhesive test or pull off test. has been done research on 6 pieces of steel material with a size of 300 mm x 300 mm x 10 mm that is blasted and measured surface roughness, cleanliness, relative humidty, surface temperature and dew point. Test piece is coated with variety of time intervals at 1 hour, 3 hours and 5 hours. From the results of the painting, be measured dry film thickness (DFT) and be tested adhesive too. After that, be done analysis effect of the time interval variation to adhesive of coating layer. From the analysis is concluded that the longer the time interval can decreased adhesive of the coating layer. But the adhesive of coating on time interval 1 hour, 3 hours and 5 hours can be accepted because exceed the ISO 16276-1 standard which is 3 Mpa. For maksimum time interval at relative humidity 70-80% that is calculated with linier equation y = -0.70875x 7.52375 can be gotten maksimum time interval is 6 hours 24 minutes


Detil Peneliti

Dosen Pembimbing 1 :Rasiawan
Dosen Pembimbing 2 : Ruddianto

Program Studi : D3 - TEKNIK BANGUNAN KAPAL
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.