ANALISIS PERBANDINGAN KEBUTUHAN ANTARA ALUMINUM ANODE DAN ZINC ANODE PADA PELAT LAMBUNG KAPAL UNTUK PENGENDALIAN KOROSI

A COMPARATIVE ANALYSIS OF ALUMINUM ANODE AND ZINC ANODE TO CONTROL CORROSION IN THE HULL PLATE SHIP

Nurul Ainun Zakina (6111030049)


Abstrak

ANALISIS PERBANDINGAN KEBUTUHAN ANTARA ALUMINUM ANODE DAN ZINC ANODE PADA PELAT LAMBUNG KAPAL UNTUK PENGENDALIAN KOROSI Nama : Nurul Ainun Zakina (6111030049) Pembimbing : Ir. Wiwik Dwi Pratiwi, MT ABSTRAK Korosi adalah penurunan mutu logam akibat reaksi elektrokimia dengan lingkungan. Hal ini tentu akan sangat merugikan terutama untuk pemilik kapal. Perlindungan katodik dengan menggunakan anoda tumbal merupakan salah satu bentuk perlindungan untuk pelat bangunan kapal terhadap korosi. Oleh karena itu, pemilihan jenis anoda dan penentuan kebutuhan jumlah anoda dengan tepat sangat penting dilakukan. Dalam menentukan jenis anoda yang tepat dan kebutuhan jumlah anoda dapat dilakukan dengan estimasi melalui observasi dari aturan-aturan yang ada, pengalaman di lapangan dan wawancara dapat dijadikan suatu pertimbangan dalam penentuan jenis anoda dan mengestimasi kebutuhan anoda tersebut. Hasil dari estimasi didapatkan kebutuhan anoda antara aluminum anode dengan zinc anode berbeda pada kapal ?KCR 60 M?. Dengan umur proteksi 2 tahun kebutuhan untuk material aluminum anode adalah 38 buah dengan penempatan 30 buah anoda pada lambung kapal dan 8 buah anoda pada rudder. Sedangkan untuk zinc anode material anoda yang dibutuhkan adalah 58 buah dengan penempatan 46 buah anoda pada lambung kapal dan 12 buah anoda untuk rudder. Berat anoda perbuah untuk aluminum anode yaitu 2,3 kg dan untuk zinc anode adalah 4,8 kg dengan dimensi yang sama PxLxT (290x100x50 mm). Biaya anoda total untuk kebutuhan aluminum anode adalah Rp 7.500.000,26 dan untuk zinc anode adalah Rp 14.897.760,29. Kata kunci : Korosi, Proteksi Katodik, Anoda Tumbal, Kebutuhan Anoda, Biaya Total, Jenis Anoda


Abstract

ANALYSIS FOR COMPARISON NEEDS ALUMINUM ANODE AND ZINC ANODE IN THE SHIP HULL PLATE FOR CORROSION CONTROL Name : Nurul Ainun Zakina (6111030049) Supervisor : Ir. Wiwik Dwi Pratiwi, MT ABSTRACT Corrosion of metals is due to a decrease in the quality of the electrochemical reaction with the environment. This would be very detrimental especially for ship owners. Cathodic protection using sacrificial anode is a form of protection for ship building plate against corrosion. Therefore, the choice of the anode and the determination of the exact number of anode needs is very important. In determining the appropriate type of anodes and anode needs can be estimated with number of estimated by observation of the existing rules, experience in the field and interviews can be used as a consideration in the determination of the anode and the anode estimating needs. The results obtained from the estimation between the anode needs of aluminum anode and zinc anode for "KCR 60 M" is different. With a design life of 2 years the need for protection of aluminum anode material is 38 pieces to 30 pieces anode placement on the ship's hull and 8 pieces of the anode on the rudder. As for the zinc anode, the anode material required is 58 pieces to 46 pieces of anode placement hull anodes and 12 pieces for the rudder. Weight apiece for aluminum anode is 2,3 kg and for the zinc anode is 4,8 kg with the same dimensions LxWxH (290x100x50 mm). The total cost of purchase of materials for the needs of the aluminum anode is Rp 7.500.000,26 and for the zinc anode is Rp 14.897.760,29. Key words: Corrosion, Cathodic Protection, Sacrificial Anodes, Anode Needs, Costs Total, Anode Type


Detil Peneliti

Dosen Pembimbing 1 :Wiwik Dwi Pratiwi
Dosen Pembimbing 2 :

Program Studi : D3 - TEKNIK PERANCANGAN DAN KONSTRUKSI KAPAL
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.