STUDI EFEKTIFITAS PWHT PADA PIPA CARBON STEEL DENGAN VARIASI JENIS SAMBUNGAN

STUDY OF PWHT EFFECTIVENESS ON CARBON STEEL PIPE WITH JOINT TYPE VARIATIONS

Sandy Pratama Vebriarianata (6110030010)


Abstrak

STUDI EFEKTIFITAS PWHT PADA PIPA CARBON STEEL DENGAN VARIASI JENIS SAMBUNGAN Nama : Sandy Pratama V (6110030010) Pembimbing : Ruddianto ST., MT. ABSTRAK Base-metal hingga daerah sekitar weld-metal cenderung mengalami transformasi setelah melalui bermacam-macam fase metalurgi. Material terutama carbon steel SA106 Gr.B akan berubah secara struktur maupun sifat karena efek dari pengelasan (pemanasan dan pendinginan). Struktur yang tidak homogen ini menyimpan banyak tegangan sisa yang membuat material memiliki sifat yang lebih keras namun ketangguhannya lebih rendah. Untuk menjadikan material pada sifat yang diinginkan terutama dalam ketangguhan maka struktur yang berubah dimodifikasi melalui PWHT pada temperatur 600?C-620?C dengan waktu pemanasan 72 menit (1,2 jam). Dengan mempertimbangkan jenis sambungan (fillet dan butt) serta waktu eksekusi PWHT (pagi dan sore), diharapkan dapat diketahui nilai efektifitas, serta faktor-faktor yang turut mempengaruhi berhasil atau tidaknya suatu proses PWHT. Secara keseluruhan jenis sambungan butt pada material pipe to pipe paling efektif dilakukan PWHT dengan penggunaan periode eksekusi pada shift 1 (pagi hari). Kata kunci: PWHT, efektifitas, SA106 Gr. B


Abstract

STUDY OF PWHT EFFECTIVENESS ON CARBON STEEL PIPE WITH JOINT TYPE VARIATIONS Name : Sandy Pratama V (6110030010) Adviser : Ruddianto ST., MT. ABSTRACT The results of the welding process on the join line between a base-metal, to the area around the weld-metal undergoes a transformation through a variety of metallurgical phase. Material especially SA106 Gr.B carbon steel will had a structural either characteristical changes due to the effects of heating and cooling. This structure is not homogeneous, also contain a lot of residual stresses that have properties to make the material harder but lower toughness. To make the material in the desired properties, especially in the toughness, the modified structure will be changed through the PWHT on temperature of 600? C to 620? C with a holding time of 72 minutes (1,2 hours). Taking into account the joint type (fillet and butt) and PWHT execution time (morning and afternoon), is expected to know the value of effectiveness, as well as the factors that influence the success or failure of a process PWHT. Overall joint type butt on the pipe to pipe material most effectively done with the use of PWHT on shift 1 execution period (during the morning) Key Words: PWHT, effectiveness, SA106 Gr. B


Detil Peneliti

Dosen Pembimbing 1 :Ruddianto
Dosen Pembimbing 2 : Ruddianto

Program Studi : D3 - TEKNIK PERANCANGAN DAN KONSTRUKSI KAPAL
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.