ANALISA CACAT HASIL PENGELASAN PIPA 6 INCH SCH. 80 CARBON STEEL MENGGUNAKAN METODE RADIOGRAFI TEST (RT

Dandy Kurniawaan, Putra (2014) ANALISA CACAT HASIL PENGELASAN PIPA 6 INCH SCH. 80 CARBON STEEL MENGGUNAKAN METODE RADIOGRAFI TEST (RT. [Tugas Akhir]

Full text not available from this repository.

Abstract

ABSTRAK Dalam sambungan pipa harus memiliki struktur konstruksi yang kuat dan terutama sambungan las nya (welding). Pada sektor HRSG(Heat Recovery Steam Generator) menggunakan pipa 6 inch sch. 80 carbon steel dengan tipe sambungan las Butt Joint. Ketidak sempurnaan dalam proses pengelasan ataupun terdapat cacat pada sambungan las pipa akan mempengaruhi keselamatan dan keamanan di area tersebut. Untuk mengetahui cacat yang timbul, maka perlu dilakukan pengujian NDT menggunakan radiografi test. Pengujian radiografi test merupakan pengujian Non Destructive Test(NDT). Proses pengujian radiografi test harus sesuai prosedur yang telah ditentukan, pengujian radiografi test menggunakan standar dari ASME section IX. Sesuai standar yang telah ditentukan, sebelum pengujian maka harus dilakukan kalibrasi alat sampai dengan proses scaning. Hal ini dilakukan bertujuan untuk mendukung kesempurnaan dalam proses pengujian NDT. Cacat yang timbul pada hasil lasan pipa 6 inch carbon steel masuk kategori kelas dari ASME section IX yang akan menentukan repair atau tidaknya sambungan las tersebut. Dari hasil analisa menunjukan sambungan las pipa 6 inch carbon steel terdapat cacat yang melebihi toleransi yang ditentukan. Hasil evaluasi menunjukan cacat lasanyang berada pada film 7-14 dimana sesuai standar penerimaan menurut ASME section IX termasuk dalam kategori cacat porosity. Kata Kunci : Carbon Steel, Non Destructive Test, ASME section IX ABSTRACT In connection pipe must have a strong construction structure and especially its welded joints (welding). In the sector of the HRSG (Heat Recovery Steam Generator) using 6 inch pipe sch. 80 carbon steel butt weld type Joint. Imperfections in the welding process or there are defects in the weld joint pipe will affect the safety and security in the area. To find defects that arise, it is necessary to NDT testing using radiographic tests. Radiographic Testing test is a test of the Non Destructive Test (NDT). Radiographic testing process should be appropriate test procedures have been specified, radiographic testing using a standard test of ASME section IX. As per the prescribed standards, testing should be performed before calibration tool until the scanning process. This is done aims to support excellence in NDT testing process. Defects that arise on the results of weld carbon steel pipe 6 inches in the category of ASME section IX class that will determine whether or not to repair the weld joint. From the analysis shows the weld carbon steel pipe 6 inches there are defects which exceed the specified tolerances. The evaluation results showed defects in the film are lasanyang 7-14 where appropriate admissions standards according to ASME section IX included in the category of porosity defects. Keywords: Carbon Steel, Non Destructive Test, ASME section IX

Item Type: Tugas Akhir
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Permesinan Kapal > D3 Teknik Permesinan Kapal
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 21 Aug 2018 04:21
Last Modified: 21 Aug 2018 04:25
URI: http://repository.ppns.ac.id/id/eprint/9

Actions (login required)

View Item View Item