ANALISA MECHANICAL PROPERTIESDAN STRUKTUR MIKRO PADA TUBE EXISTINGA-312 TP347 DENGAN VARIASI FILLER METALMENGGUNAKAN PROSES PENGELASAN GTAW

Febri, kurniadani (2014) ANALISA MECHANICAL PROPERTIESDAN STRUKTUR MIKRO PADA TUBE EXISTINGA-312 TP347 DENGAN VARIASI FILLER METALMENGGUNAKAN PROSES PENGELASAN GTAW. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

Material stainless stell merupakan material yang memiliki sifat mekanik yang sangat baik. Namun pada penggunaan yang terus-menerus dapat membuat material tersebut mengalami kebocoran. Proses repair menggunakan existing material harus dioptimalkan karena keterbatasan pada penggunaan material baru. Contohnya pada material tube existing A312 TP347. Pada boiler hal ini sangat sering terjadi, sehingga proses repair menggunakan existing material dengan metode yang benar sangat dibutuhkan. Proses pengelasan yang digunakan adalah proses las gas tungsten arec welding dengan variasi filler metal yang berbeda. filler metal yang digunakan adalah ER308, ER309 dan ER316 dengan tipe penyambungan butt joint.Perbedaan filler metal yang digunakan pada proses pengelasan akan di bandingkan weld metalnya. Hasil pengujian menunjukkan dari tiga filler metal, didapatkan dari data pengujian bending keseluruan material dapat di terima. Dari pengujian tarik individual didapatkan bahwa pengelasan yang menggunakan fillerER316 paling tinggi, adalah specimen nomer enam yaitu sebesar 584,66 MPa. Sedangkan kekuatan tarik yang paling rendah adalah spesimen nomer dua yaitu yang menggunakan filler ER 308 sebesar 474,06 MPa. Sedangkan dari nilai rata-rata kekuatan tarik yang tertingididapatkan dari fillerER309 sebesar 563,3 MPa dan yang paling terendah didapatkan dari filler ER 308 sebesar 532.91MPa. Dari data pengujian kekerasan pada daerah Weld metal yang paling tinggi didapatkan dari filler ER309.Dari nilai rata-rata tak jauh beda dengan filler ER308 danER316. Pada pengujian struktur mikro di daerah BM terbentuk pola karbida krom, sedangkan di daerah head affected zonedan fusion line pola karbida krom mulai berkurang atau memudar tidak segelap daerah base metal. Kata Kunci : Material tube existingA-312 TP347, GTAW, Variasi logam pengisi, Sifat mekanik, Struktur mikro Stainlessnsteel material is material which have mechanical propertiss very good. But in continous using can make the material run into leakge.repair process using existing material shold be optimized, because limitation on using of new material.tehe example in the tube of existing material A-312 TP347 .in the boiler this case is often happeng, so the repair using existing material with the right method very needed. Welding process which used is GTAW welding process with variation of different filler matal, filler metal which used is ER308, ER309 and ER316 with joint type butt joint. The different of filler metal that used for welding process will compared the weld metal. The result of test from three filler metal, was found from all of bending test data material could be accepted. From individual tensile test was found that welding which using filler ER316 is the highest is 6 the specimen that is 586,66 MPa. Whereas the lowest tensile strength is 2 and specimen with 474,06 MPa. Whereas from the higherst average of value tensil strength available from filler ER309 with563,3 MPa and the lowest available from filler ER308 with 532,91 MPa. From the hadness test data in the weld metal zone the highest available from filler ER309. From the average value not much ditterent with filler ER308 and ER316. On micro structure examihation in the base metal zone formed chrome carbide seheme, whereas in the HAZ zone and FL the chrome carbide scheme set to decrease or dim not as dark as BM zone. Keywords: material tube existing A-312 TP347, GTAW, variation filler matal, mechanical propertiss, micro structure

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 25 Aug 2018 03:07
Last Modified: 25 Aug 2018 03:07
URI: http://repository.ppns.ac.id/id/eprint/83