ANALISIS PENGARUH DEFORMASI PLASTIS TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO PENGELASAN ALUMINIUM PADUAN 5083 DENGAN 6061

Jean Drea Vombrie, Fistony (2014) ANALISIS PENGARUH DEFORMASI PLASTIS TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO PENGELASAN ALUMINIUM PADUAN 5083 DENGAN 6061. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Pada umumnya cukup banyak perlakuan yang diberikan terhadap material sebelum dilakukan pengelasan untuk mendapatkan bentuk dan ukuran yang sesuai dengan bagian yang diinginkan. Salah satunya dengan proses deformasi plastis. Akibat perlakuan tersebut material akan mengalami perubahan bentuk dari struktur mikro dan sifat mekaniknya serta adanya kemungkinan mengalami crack. Dalam penelitian ini, peneliti menggunakan sambungan pengelasan logam tak sejenis antara aluminium paduan 5083(non heatreateble) dengan 6061(heatreateble). Dilakukan proses strain hardeningpada Aluminium paduan 6061 dengan 5083. Pengelasan Butt Jointdan fillet joint (T joint)aluminium tak sejenis ini menggunakan proses GMAW. Dari penelitian ini, proses strain hardeningyang dilakukan dapat meningkatkan nilai kekerasan pada base metal 5083,sedangkan pada aluminium 6061 kenaikan terjadi padadaerah HAZ Kata-kata kunci : aluminium 5083 dan 6061, GMAW,Strain Hardening. ABSTRACT Generaly, there are so many ways of treatment to the material before the weld to get the size and shape that welder wanted. One of the processes is deformation plastis. Deformation plastis will change the shape of micro structure, the mechanical characteristic and the possibilitiesof cracking. In this research, researcher connects the dissimilar material between aluminium 5083 (non heatreteble) with 6061 (heatreteble). The hardening process is applied towards aluminium 6061 and 5083. Butt joint weld and fille joint (T joint) aluminium used GMAW process. From this research, strain hardening process will increase the harden value of base metal 5083 meanwhile Haz area in the aluminium 6061 will increase too. Keyword : aluminium 5083 and 6061, GMAW,Strain Hardening.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > D4 Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 25 Aug 2018 03:04
Last Modified: 25 Aug 2018 03:04
URI: http://repository.ppns.ac.id/id/eprint/82