ANALISA BIAYA DAN PENGARUH PROSES METAL REMOVAL TERHADAP KETANGGUHAN SERTA PENGUJIAN RADIOGRAFI PADA MATERIAL BAJA KARBON KI-A MENGGUNAKAN PROSES SMAW

Iqbal, Fatchul Yuniardi (2016) ANALISA BIAYA DAN PENGARUH PROSES METAL REMOVAL TERHADAP KETANGGUHAN SERTA PENGUJIAN RADIOGRAFI PADA MATERIAL BAJA KARBON KI-A MENGGUNAKAN PROSES SMAW. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Metal removal adalah proses dimana menghilangkan logam dalam pengelasan yang bertujuan untuk merepair sambungan las ataupun untuk membuat alur lasan baru sehingga memudahkan pengelasan kembali pada daerah tersebut. Dalam prosesnya, metal removal memiliki beberapa metode dimana membutuhkan alat yang berbeda pada setiap prosesnya. Diantaranya menggunakan gerinda, pneumatic chisel, plasma gouging, dan carbon electrode. Pada tugas akhir ini penulis mengambil 3 metode yaitu Pneumatic Chisel, Plasma Gouging, dan Carbon Electrode untuk diteliti dan dibandingkan hasil dalam hal kualitas lasan dan analisa biaya yang dibutuhkan untuk menjalankan setiap metodenya. Dalam pengerjaannya langkah awal yang dilakukan penulis adalah melakukan pengelasan pada material KI-A dengan I joint/square groove yang nantinya di sisi sebaliknya akan dilakukan proses metal removal agar terbentuk alur lasan baru untuk selanjutnya dilakukan pengelasan pada daerah tersebut. Setelah proses pengelasan dan pengerjaan metal removal selesai dilakukan pengujian penetrant yang diaplikasikan pada daerah hasil metal removal sebelum dilakukan proses pengelasan pada daerah tersebut. Selanjutnya dilakukan pengujian radiografi dan uji impact pada specimen uji dan yang terakhir dilakukan analisa biaya terhadap ketiga metode. Hasil pada proses penelitian ini diketahui hasil pengujian penetrant pada daerah metal removal tidak ada indikasi crack. Untuk hasil radiografi tidak ada hasil yang accepted menurut ketentuan standart ASME IX. Sedangkan untuk nilai impact pada metode Pneumatic Chisel pada suhu normal di dapat rataan 1.68 J/mm 2 dan pada suhu rendah 0.61 J/mm 2 , pada penggunaan metode Plasma Gouging didapat nilai impact strength pada suhu norml sebesar 1.16 J/mm 2 dan pada suhu rendah sebesar 0.37 J/mm 2 , dan untuk metode menggunakan Carbon Electrode di dapat nilai impact strength pada suhu normal sebesar 0.87 J/mm 2 dan pada suhu rendah sebesar 0.23 J/mm 2 . Sedangkan untuk analisa biaya didapat bahwa harga penggunaan Pneumatic Chisel lebih murah dibanding Carbon electrode dan Plasma gouging menjadi metode yang paling banyak membutuhkan biaya. Kata kunci : Metal removal , pneumatic chisel, plasma gouging, carbon electrode, KI-A, SMAW ABSTRACT Metal removal is the process whereby deprive of metal in welding aimed at merepair connection las or to make the grooves welds new which makes it easy for welding back to the area. In the process, metal removal have some method where need instrument differ between each the process.Including using grinding, pneumatic chisel, plasma gouging, and carbon electrode. In this final task, the writer take 3 method is pneumatic chisel , plasma gouging , and carbon electrode for examination and compared results in terms of quality trusses and analysis of budget needed to run every the methods. In the construction the first step was done by the writer is doing welding in the material ki-a with i joint / square groove which will in the reverse side will process was completed metal removal that formed a groove welds new to next done welding at the area . After the welding and the metal removal completed testing penetrant applied for a metal before the removal done process welding at the area. Further testing radiography done and the impact on specimen test and final analysis of the method costs. Outcomes researched process is known to the testing penetrant at the metal removal there is no indication crack.To yield radiography no result that accepted according to the rules standart asme ix. While to value impact on method pneumatic chisel at normal temperatures in be rataan 1.68 j / mm2 and at low temperatures 0.61 j / mm2, on the use of plasma method gouging gained strength the impact on the temperature norml of 1.16 j / mm2 and at low temperatures of 0.37 j / mm2, and to methods of using carbon electrode in got the impact strength at normal temperatures of 0.87 j / mm2 and at low temperatures of 0.23 j / mm2. As for cost analysis found that the price of the use of pneumatic chisel cheaper than carbon electrode and plasma gouging being method most cost. 1 Key words : Metal removal , pneumatic chisel, plasma gouging, carbon electrode, KI-A, SMAW

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 17 Sep 2018 02:41
Last Modified: 17 Sep 2018 02:41
URI: http://repository.ppns.ac.id/id/eprint/795

Actions (login required)

View Item View Item