PENGARUH VARIASI KOMBINASI FILLER METAL INCONEL 625, ER309L, ER70S-6 DAN ER316 PADA PIPA API 5L Gr.X52 INSIDE OVERLAY INCOLOY 825 GTAW TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO

Gandris Azar, Sarasi (2014) PENGARUH VARIASI KOMBINASI FILLER METAL INCONEL 625, ER309L, ER70S-6 DAN ER316 PADA PIPA API 5L Gr.X52 INSIDE OVERLAY INCOLOY 825 GTAW TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

Pada pipa tipe API 5L Grade X52 yang termasuk carbon steel dan dioverlay pada bagian dalam dengan menggunakan Incoloy 825 untuk ketahanan korosi karena aliran gas, dan dilas menggunakan filler metal ER NiCrMo-3 (inconel 625) proses kombinasi GTAW. Hal ini ditujukan untuk menghasilkan hasil pengelasan yang memenuhi spesifikasi sesuai standar. Karena material nickel base alloys mempunyai harga relatif tinggi, untuk efisiensi biaya, dicoba penggunaan kombinasi filler metal stainless steel tipe ER309L dan ER316 serta carbon steel ER70S-6. Untuk metode kombinasi ini, root sebanyak 3 layer menggunakan inconel 625 dan layer 3 sampai terakhir diganti dengan kombinasi tipe ER309L, ER316 dan carbon steel ER70S-6. Untuk pengujian meliputi radiografi, tensile test, bending test, nick-break dan metallografi serta estimasi biaya per meter. Dari hasil pengelasan dan pengujian spesimen variasi kombinasi filler metal menghasilkan output berupa WPS dan PQR. Dari hasil pengujian radiografi ditemukan crack pada kombinasi ER70S-6. Dari estimasi biaya perbedaan yang jauh ditunjukkan masing-masing kombinasi ini dengan yang menggunakan full Inconel 625 dan didapatkan biaya per meter terefisien adalah kombinasi ER70S-6 namun beresiko terjadi crack sehingga dari seluruh pengujian, kombinasi alternatif yang paling recommended adalah kombinasi ER316. . Kata kunci : filler metal, incoloy, inconel, stainless steel, carbon steel, kombinasi, sifat mekanik, struktur mikro, biaya On the type of pipe API 5L Grade X52 which includes carbon steel and overlayed inside using Incoloy 825 for corrosion resistance due to the gas flow, and welded using a filler metal NiCrMo ER-3 (Inconel 625) combination GTAW process. It is intended to produce results that meet the specifications of the appropriate welding standards. Because the material nickel base alloys have relatively high prices, for cost efficiency, attempted use of a combination of stainless steel filler metal type and ER316 ER309L and carbon steel ER70S-6. For this combination method, the root as much as 3 layers using Inconel 625 and 3 until the last layer is replaced by a combination of type ER309L, ER316 and carbon steel ER70S-6. For the testing is radiographic testing, tensile test, bending test, nick-break and metallografi as well as the estimated cost per meter. From the results of the test specimen variation welding and filler metal combination produces an output in the form of WPS and PQR. Radiographic examination of the results found crack in combination ER70S-6. Of the estimated costs that much difference indicated respectively by each of combination with full Inconel 625 and obtained cost per meter is the most efficient combination of ER70S-6 but a risk of crack that of the entire test, the combination of the most recommended alternative is a combination of ER316. Keywords: filler metal, incoloy, inconel, stainless steel, carbon steel, combination, mechanical properties, microstructure, costs

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 25 Aug 2018 02:47
Last Modified: 25 Aug 2018 02:47
URI: http://repository.ppns.ac.id/id/eprint/79

Actions (login required)

View Item View Item