PENGARUH FLOWRATE HIGH PURITY DAN ULTRA HIGH PURITY TERHADAP SIFAT MEKANIK PADA PENGELASAN ALUMINIUM PADUAN 5083 H116

Mushoffa, Ahda (2016) PENGARUH FLOWRATE HIGH PURITY DAN ULTRA HIGH PURITY TERHADAP SIFAT MEKANIK PADA PENGELASAN ALUMINIUM PADUAN 5083 H116. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Dalam setiap proses pengelasan apapun, tidak menutup kemungkinan untuk terjadinya cacat las, adalah kemungkinan terjadinya kesalahan sangatlah besar dan dapat berakibat fatal. Kesalahan proses pengelasan dapat terjadi karena banyaknya material yang akan menimbulkan kemungkinan terjadinya defect. dalam penelitian ini saya membedakan dua variable yaitu pengaruh gas pelindung argon high purity, ultra high purity dan perbedaan flowrate. Karena aluminium dan paduan aluminium mempunyai sifat yang kurang baik bila dibandingkan dengan baja, diantaranya adalah mempunyai panas jenis dan daya hantar yang tinggi, mudah teroksidasi dan membentuk oksida aluminium AL2O3 yang mempunyai titik cair yang tinggi sehingga mengakibatkan peleburan antara logam dasar dan logam las menjadi terhalang, dan bila mengalami proses pembekuan yang terlalu cepat akan terbentuk rongga halus. Kata Kunci: Aluminium,Gas Argon High Purity dan UHP, Flowrate ABSTRACT In any welding process whatsoever, do not rule out the possibility of the occurrence of weld defects, is the risk of error is very large and can result in failure. Welding process errors can occur because of the material that will give rise to the possibility of the occurrence of the defect. in this study I distinguish between two variables that influence the protective gas argon high purity, ultra high purity and flowrate difference. Because aluminum and aluminum alloys have properties that are less well when compared with steel, such as having specific heat and conductivity are high, easily oxidized and form aluminum oxide Al2O3 which has a high melting point, resulting in a fusion between the base metal and weld metal becomes blocked and when experience rapid cooling process is too fast will form a smooth cavity. KeyWord: Aluminium,Gas Argon High purity and UHP, Flowrate

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 17 Sep 2018 01:46
Last Modified: 17 Sep 2018 01:46
URI: http://repository.ppns.ac.id/id/eprint/787

Actions (login required)

View Item View Item