Pratama, Agung Faris (2016) PENGARUH PENGULANGAN BAKING OVEN PADA ELEKTRODA LOW HYDROGEN TERHADAP SIFAT MEKANIK. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.
Full text not available from this repository.Abstract
ABSTRAK Pengelasan SMAW (shielded metal arc welding) adalah pengelasan yang menggunakan proses panas yang terjadi akibat lompatan elektron dari elektroda dan base metal, jenis-jenis elektroda berselaput sendiri ada berbagai macam jenis salah satunya adalah elektroda low hydrogen, elektroda hidrogen rendah elektroda, sangat mudah menyerap kebasahan dalam perlakuan elektroda low hydrogen harus sangat teliti, elektroda harus di oven sebelum digunakan. Pada flow chart pengembalian elektroda pada PT.BBI, penggunaan baking oven pada elektroda low hydrogen hanya boleh dilakukan hanya 1X pengulangan. Penelitian dengan melakukan perlakuan penggunaan baking oven 1X , 2X, dan 3X menggunakan material SA-36, dengan menggunakan elektroda low hydrogen tipe E-7018. Penelitian dilakukan dengan menarik hasil uji radiografi, uji tensile, uji bending, uji hardness. Dari data hasil uji tarik dan grafik tegangan-regangan nilai rata-rata kuat tarik pada pengulangan baking oven 1X ini sebesar rata-rata 515.74 MPa sedangkan pada pengulangan baking oven 2X dan pengulangan baking oven 3X nilai rata-rata kuat tariknya hanya sebesar 543.24 MPa dan 565.05 MPa. Nilai kekerasan material semakin tinggi, dan dari Hasil visual dari uji bending diatas dapat dianalisa bahwa ada cacat pada spesimen A2, C2, B2 dengan ukuran yang masih bisa diterima menurut ASME Sec IX, sementara pada spesimen C1 ditemukan cacat sebesar 3 mm yang timbul, Sehingga spesimen uji C1 (baking oven 3x) dinyatakan rejected. Kata Kunci : SMAW, uji radiografi , uji tarik , uji lengkung , uji kekerasan ABSTRACT SMAW ( shielded metal arc welding) is welding using a process heat due of electrons from elecrtrodes and base metal, the types of electrodes welding own any of various kinds, one of them is a electrodes low hydrogen, in flow chart return of electrodes in PT BBI, used of baking oven electrodes low hydrogen may only be conducted just once repetition, electrodes have to be in heat in an oven before use. In this research by doing a threatment using of baking oven once, twice, and three times.Using plate SA-36, with use a electrodes low hydrogen type E-7018. In this research was done with a conclusion from radiography test,tensile test, bending test, hardness test. According to data from tensile test and charts stress – strain the average value of the tensile test on the repetition of baking oven 1x is 515.74 Mpa whilw in repetition baking oven 2X and 3X the average value is 543.24 Mpa and 565.05 Mpa, From the data the result a hardness is increasing. In result of visual bending test can be analysed that there is a defect in a specimen A2, C2, B2 with size 1mm, 2mm, 2mm which can be accepted according to ASME sec IX, and in specimen C1 ( baking oven 3X) was it be rejected. Key Word : SMAW, radiography test , tensile test , bend test , hardness test
| Item Type: | Thesis (Diploma) |
|---|---|
| Subjects: | T Technology > T Technology (General) |
| Divisions: | Jurusan Teknik Bangunan Kapal > D4 Teknik Pengelasan |
| Depositing User: | Unnamed user with email repository@ppns.ac.id |
| Date Deposited: | 15 Sep 2018 05:03 |
| Last Modified: | 15 Sep 2018 05:03 |
| URI: | http://repository.ppns.ac.id/id/eprint/783 |
Actions (login required)
 |
View Item |