PENGARUH VARIASI KUAT ARUS DAN JARAK KAMPUH LAS TERHADAP KEKUATAN TARIK DAN STRUKTUR MIKRO PADA MATERIAL 5083.

WAHYUDI, QOLEK (2016) PENGARUH VARIASI KUAT ARUS DAN JARAK KAMPUH LAS TERHADAP KEKUATAN TARIK DAN STRUKTUR MIKRO PADA MATERIAL 5083. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Perkembangan pada dunia kontruksi kini berjalan dan berkembang semakin pesat. Pada umumnya pengelasan dilambung kapal mengunakan kampuh V tetapi pemilihan kampuh tersebut akan memakan waktu pengerjaan, untuk meminimalisir proses pembangunan sebuah kapal. Pada perusahaaan tersebut memilih mengunakan kampuh I. Ditinjau dari efesiensi pengunaan yaitu mempersingkat waktu dan biaya. Pada penilitian ini akan mengunakan material aluminium 5083 yang dikerjakan dengan mesin las GMAW dan mengunakan filler metal ER.5356 dengan tiga variasi kuat arus yaitu 150A, 160A, dan 170A, serta tiga variasi gap yang berbeda yaitu 2mm,3mm, dan 4mm. pengujian yang akan dilakukan adalah uji tarik, uji mikro, dan uji makro. Dari hasil pengujian tarik dapat dilihat semakin tinggi kuat arus yang semakin tinggi kuat arus yang digunakan maka semakin rendah kuat tariknya. Dan bedasarkan pengujian makro dapat dilihat semakin tinggi dengan bertambahnya gap namun dilusi yang terjadi semaki rendah,dilusi yang tinggi didapat dengan cara menaikan kuat arus. Sedangkan hasil pengujian mikro dapat di lihat arus yang tinggi akan menyebabkan banyaknya mg2si yang terbentuk. Hal ini menurunkan kuat Tarik. Kata-kata kunci : GMAW, Kuat Arus, Material Aluminium 5083. ABSTRAC The construction work field is growing and developing more rapid nowadays. Generally the welding process on ship full using v groove joint design but actually based on the research that kind of joint design takes a lot of time to be done. So to minimalize time of work, decided to choose joint desing types I due to its efficiency of work time and costs. In this research the material being used was aluminium 5083 that welded by Gas Metal Arc Welding (GMAW) process and the filler metal used was ER5356. There were three current variations of this research, which are using 150A, 160A, and 170A. And also there were three gap variations which are using gap 2mm, 3mm, and 4mm. The tests that took for this research were tensile test, micro structure test, and macro etch test. The result of tensile test is higher the current, the lower the tensile strength. And based on the macro etch test known that the wider the gap, the smaller the dilution of weld metal. The last, on the micro test know that the higher the current of welding process, the forming of mg2si is going faster which is makes the tensile strength going low. Keywords: GMAW, Tensile Strength, Material Aluminium 5083.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 15 Sep 2018 04:23
Last Modified: 15 Sep 2018 04:23
URI: http://repository.ppns.ac.id/id/eprint/778

Actions (login required)

View Item View Item