ANALISA PERUBAHAN SIFAT MEKANIK DAN STRUKTUR MIKRO MATERIAL PIPA SUPERHEATER 13CrMo44 BOILER YOSHIMINE 1 PG. GEMPOLKREP MUSIM GILING TAHUN 2008-2012

Febry Fajar, Fanany (2014) ANALISA PERUBAHAN SIFAT MEKANIK DAN STRUKTUR MIKRO MATERIAL PIPA SUPERHEATER 13CrMo44 BOILER YOSHIMINE 1 PG. GEMPOLKREP MUSIM GILING TAHUN 2008-2012. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

Pada penelitian ini dilakukan analisa secara teknis perubahan sifat mekanik dan struktur mikro yang terjadi pada material 13CrMo44 pemakaian 5 tahun (2008-2012) dengan akumulasi waktu opersional selama 21.600 jam, temperatur operasional 550 0 C-600 0 C, tekanan kerja maksimal 25 kg/cm 2 dan temperatur uap rata-rata sebesar 330 0 C. Dengan mengunakan data pembanding material 13CrMo44 baru selama proses pengujian dan analisa. Proses pengujian yang dilakukan dalam penelitian ini adalah pengujian visual, pengujian positive material identification (PMI), pengujian metallografi, pengujian kekerasan, dan pengujian tarik. Penelitian pada material 13CrMo44 pemakaian 5 tahun dibandingkan 13CrMo44 baru membuktikan pada pengujian visual ditemukan terjadinya korosi pada outside surface dan endapan kerak (scale) yang memiliki ketebalan rata-rata 2,2 mm pada inside diameter pipa. Pada pengujian PMI terjadi kenaikan kandungan karbon sebesar 0,03% dan penurunan Cr sebesar 0,66%. Pada pengujian metallografi terjadi pembesaran butiran pearlite dan terbentuknya endapan karbida Mo 2C dan Cr7C3 pada butiran ferrite dan pada batas butir. Pada pengujian tarik terjadi kenaikan kuat tarik rata-rata sebesar 40,58 Mpa. Dan pada pengujian kekerasan terjadi kenaikan nilai kekerasan pada outside surface rata-rata sebesar 22,7 HV dan pada inside surface rata-rata sebesar 13,1 HV. Terjadi kenaikan kuat tarik setiap tahunya sebesar 115,86 Mpa. Dan dapat disimpulkan material 13CrMo44 pemakaian 5 tahun masih dapat digunakan kembali dalam iv proses opersional 1 tahun kedapan karena masih dalam batas kuat tarik yang diijinkan standart DIN 17175. Kata kunci : Material 13CrMo44, Pipa Superheater, Pengujian Visual, PMI, Pengujian Metallografi, Pengujian Tarik, Pengujian Kekerasan. In the reaserch, the analysis was done technically on the mechanical properties and micro structural change that occurred in the material of 13CrMo44 which has been used for 5 years (2008-2012) with accumulation of time temperature over 21.600 hours, operational temperature by an average 550 0 C – 600 0 C, maximum working pressure 25 kg/cm 2 and steam temperature by an average 330 0 C. By using comparative data of new material 13CrMo44 during the process of the testing and analysis. The testing process carried out in this reaserch was a visual test, positive material identification test (PMI), metallography test, tensile test and hardness test. The reaserch on material 13CrMo44 which has been used for years finally proved that in visual testing, corrosion was found on the outside surface and sediment scale which had average thickness of 2,2 mm in the inside diameter pipe. At the PMI testing there was an increase carbon content 0,03% and decrease chromium content 0,66%. In metallography testing there was enlargemen of pearlite grain and formation carbide Cr7C3 and Mo2C in the ferrite grains and at grain boundaries. In tensile test, there was an increase of tensile strength average 40,58 Mpa. And in the hardness testing there was an increase of hardness value on the outside surface average 22,7 HV and on the inside surface average 13,1 HV and increase tensile strength every years average 115,86 Mpa. And the conclusion material of 13CrMo44 which has been used for 5 years can vi operational 1 years again because tensile strength not exceed range standart DIN 17175. Keyword: Material 13CrMo44, Superheater Pipe, PMI, Metallography test, Tensile test, Hardness test

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 24 Aug 2018 06:55
Last Modified: 24 Aug 2018 06:55
URI: http://repository.ppns.ac.id/id/eprint/74