PENGARUHSOLUTION TREATMENT PADA HASIL PENGELASAN OVER HEAT INPUT PADA MATERIAL SA240 TYPE 304 TERHADAP KEKERASAN DAN KEPEKAAN INTERGRANULAR CORROSION ATTACK

M Afif, Syaichoni (2014) PENGARUHSOLUTION TREATMENT PADA HASIL PENGELASAN OVER HEAT INPUT PADA MATERIAL SA240 TYPE 304 TERHADAP KEKERASAN DAN KEPEKAAN INTERGRANULAR CORROSION ATTACK. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

Dalam dunia Industri, Manufaktur maupun fabrikasi terutama dalam proyek pembangunan suatu perusahaan, Salah satunya dalam proyek pembangunan pabrik PT. PETRO JORDAN ABADI yang terdapat proses fabrikasi item converterdengan menggunakan material austenitic stainless steel (SA 240 Type 304), dan filler metal yang digunakan yaitu E308 / 308H-16 dengan proses pengelasan SMAW. Namun dalam penggunaan aplikasinya terdapat korosi intergranular yang dikarenakan karbida krom yang terjadi akibat hasil pengelasan over heat input, untuk memperbaiki karbida krom yang telah terjadi maka diperlukan perlakuan solution treatmentdengan tujuan untuk melarutkan karbida krom yang telah terjadi.. Pada penelitian ini dilakukan pada3 variabel proses solution treatmentantara lainsolution treatmenttemperature 850⁰C, 900⁰C, dan950⁰C yang diaplikasikan pada hasil pengelasan.kemudian dilakukan pengujian kekerasan vickers dan pengujian korosi intergranular berdasarkan standart ASTM A 262 practice B. Hasil dari penelitian ini menjelaskan bahwa solution treatment temperature 950⁰C mengakibatkan terjadinya penurunan kekerasan dan kepekaan terhadap serangan korosi intergranular. Penelitian ini nantinya akan bermanfaat sebagai refrensi bagi industri maupun fabrikasiterutama bagi PT. PETRO JORDAN ABADI. Kata kunci :Material SA 240 Type 304, Solution treatment, pengelasanover heat input, korosi intergranular. On the Industrial, Manufacturingand on sitefabricationespecially on the company building project, such as plant project on PT. PETROJORDANABADIwhich is containedfabricationprocessfor converter itemsthat used austeniticstainless steel(SA 240Type304) materials, and thefillermetalused isE308/308H-16 with theSMAWweldingprocess. However,on its application there aresomeintergranular corrosioncaused the over heat input on welding result so there arechromium carbide inside it.Torepair thechromium carbidethathasbeen occurs,thesolution treatmentbecomes the best solutionto dissolve thechromium carbide. This researchconducted to3solution treatment variables process that is solution treatmentfor 850⁰C, 900⁰Cand950⁰Cthatapplied to theweldment. Then do such a hardnesvickers testandintergranular corrosiontestbased onASTM A262practiceB. The resultofthis expertment will be explainthat thesolution treatmentfor950⁰Ccaused decreasing of hardnessandsusceptibility tointergranularcorrosionattack. This experiment will be the beneficialreferencesfor the industrialand fabrication, especially for PT. PETROJORDANABADI. Keywords :MaterialSA240Type304, Solutiontreatment, over-heat input welding, intergranularcorrosion.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 24 Aug 2018 06:42
Last Modified: 24 Aug 2018 06:42
URI: http://repository.ppns.ac.id/id/eprint/70

Actions (login required)

View Item View Item