STUDI PEMANFAATAN LIMBAH SANDBLASTING SEBAGAI BAHAN PEMBUATAN BATAKO STUDI KASUS : PT. XYZ

Irlanda, Vyke Ayu (2016) STUDI PEMANFAATAN LIMBAH SANDBLASTING SEBAGAI BAHAN PEMBUATAN BATAKO STUDI KASUS : PT. XYZ. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Limbah sandblasting termasuk salah satu limbah B3 (Bahan Berbahaya dan Beracun) yang dihasilkan dari proses penyemprotan material steel grit ke permukaan. PT. XYZ merupakan salah satu industri yang menghasilkan limbah sandblasting. Paparan limbah sandblasting dalam waktu tertentu dapat menyebabkan penyakit ganguan pernafasan yaitu silicosis. Oleh karena itu perlu dilakukan pemanfaatan limbah sandblasting dengan solidikasi salah satunya dengan dijadikan batako. Tujaan penelitian ini untuk mengidentifikasi hasil kuat tekan, resapan, menganalisis hasil TCLP dan komposisi terbaik batako menggunakan limbah sandblasting. Limbah sandblasting pada penelitian dijadikan sebagai pengganti pasir. Dalam penelitian ini material yang digunakan dalam pembuatan batako dilakukan uji material berupa uji berat jenis, kadar air, resapan, dan kebersihan material terhadap lumpur. Perbandingan material yang digunakan 1:2:3 semen:pasir:abu batu. Komposisi campuran limbah sandblasting yang digunakan 15%, 30%, 45%, dan 60% sebagai pengganti pasir. Berdasarkan hasil penelitian diperoleh hasil kuat tekan pada komposisi 0%, 15%, 30%, 45%, dan 60% sebesar 62 kg/cm 2 , 63 kg/cm 2 , 44 kg/cm 2 , 66 kg/cm 2 , dan 69 kg/cm 2 . Penggantian pasir dengan limbah sandblasting menghasilkan batako dengan kuat tekan yang semakin tinggi yang memiliki mutu II kecuali pada komposisi 30% dan memiliki nilai resapan air yang semakin rendah kecuali pada komposisi 15%. Hasil resapan air pada komposisi 0%, 15%, 30%, 45%, dan 60% sebesar 8%, 9%, 7%, 6,78%, dan 6,07%. Komposisi terbaik batako dengan menggunakan limbah sandblasting sebagai pengganti pasir pada penelitian ini terdapat pada komposisi 60% dengan nilai kuat tekan 69 kg/cm 2 , nilai resapan 6,07% dan hasil uji Toxicity characteristic leaching procedure (TCLP) yang telah sesuai dengan baku mutu yang telah ditetapkan. Kata kunci : Batako, Kuat Tekan, Resapan, Sandblasting, Silicosis. ABSTRACT Sandblasting waste is one of the hazardous waste which is a result of a process of spraying material steel grit to the surface. PT. XYZ is one of the industries that produce sandblasting waste. Exposure of sandblasting waste for a long time can cause respiratory disorder which is silicosis. Therefore it is necessary to utilize sandblasting waste using solidification process by creating bricks. The objective of this study is to examine the results of compressive strength, absorption, the brick TCLP test results and the best composition using sandblasting waste. Sandblasting waste in the study area is served as a substitute for sand. In this study the material uses in brick-making material in the form of test density, moisture content, infiltration, and the cleanliness of the material to the sludge. Comparison of the material used 1: 2: 3 cement: sand: stone gray. The composition of the mixtures are used sandblasting waste 15%, 30%, 45%, and 60% as a substitute for sand. Based on the research results compressive strength in the composition of 0%, 15%, 30%, 45%, and 60% at 62 kg / cm 2 , 63 kg / cm 2 , 44 kg / cm 2 , 66 kg / cm 2 , and 69 kg / cm 2 . Replacement of waste sandblasting sand to produce concrete blocks with higher compressive strength which has quality II except in a composition of 30% and has a value of water absorption is lower than on the composition of 15%. Results of water absorption on the composition of 0%, 15%, 30%, 45%, and 60% of 8%, 9%, 7%, 6.78% and 6.07%. The best composition sandblasting brick by using waste as a substitute for sand in this study contained in the composition of 60% to the value of the compressive strength of 69 kg / cm 2 , absorption value 6.07% and the Toxicity Characteristic Leaching Procedure (TCLP) which complies with the quality standards has been established. Keywords: Brick, Compressive Strength, Absorption, Sandblasting, Silicosis.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Teknik Keselamatan dan Kesehatan Kerja
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 14 Sep 2018 03:34
Last Modified: 14 Sep 2018 03:34
URI: http://repository.ppns.ac.id/id/eprint/684

Actions (login required)

View Item View Item