Pengaruh Teknik Temper Bead Welding (Alternate Temper Bead Technique dan Weld Toe Tempering Technique) Sebagai Pengganti Proses PWHT pada Material SA 516 Grade 70 Terhadap Sifat Mekanik dan Struktur Mikro

Singgih, Pujiantoro (2014) Pengaruh Teknik Temper Bead Welding (Alternate Temper Bead Technique dan Weld Toe Tempering Technique) Sebagai Pengganti Proses PWHT pada Material SA 516 Grade 70 Terhadap Sifat Mekanik dan Struktur Mikro. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

Teknologi pengelasan dalam pembuatan pressure vessel saat ini sangat berkembang dengan pesat dimana untuk memperoleh hasil pengelasan yang berkualitas maka dilakukan perlakuan khusus pada pressure vessel tersebut diantaranya yaitu proses Post Weld Heat Treatment (PWHT). Proses PWHT wajib dilakukan terutama dalam proyek-proyek Oil & Gas, Petrochemical, Power Plant, dan lain-lain. Menurut Welding Technology Institute of Australia (WTIA), salah satu cara untuk menghindari proses PWHT yang membutuhkan biaya operasi lebih mahal yaitu dengan teknik Temper Bead Welding (TBW). Dalam penelitian ini akan membandingkan hasil dari proses PWHT dengan hasil dari proses Temper Bead Welding dengan metode Alternate Temper Bead Technique dan Weld Toe Tempering Technique. Material yang digunakan untuk spesimen pengujian adalah SA 516 grade 70 dengan proses pengelasan GMAW. Proses perlakuan PWHT tersebut dilakukan pemanasan dalam furnace dengan suhu 595 o C lalu dengan holding time selama 1 jam. Teknik pengelasan dari hasil 2 metode diatas dibandingkan dengan beberapa pengujian melalui hasil pengujian hardness, impact, dan struktur mikro untuk memastikan bagaimana pengaruh metode temper bead welding bisa menggantikan proses perlakuan PWHT. Hasil yang didapat dari penelitian ini adalah dilihat dari struktur mikro yang terjadi pada daerah HAZ menjadi fine grain. Jika dihubungkan dengan nilai kekerasan maka yang terjadi akan menjadi lunak diakibatkan proses temper ya ng terjadi pada daerah HAZ. Dengan rata-rata nilai kekerasan pada PWHT 170,12 HVN, pada alternate temper bead technique 212,47 HVN, pada weld toe tempering technique 221,21 HVN. Hal tersebut dapat terlihat selisih nilai kekerasan proses temper bead welding jauh lebih besar dengan proses PWHT. Sedangkan pengujian impact pada suhu -15 o C selisih paling besar antara PWHT 1,5 J/mm 2 dan proses temper bead technique metode weld toe tempering technique 0,94 J/mm 2 dengan selisih 0,56 J/mm 2 . Dengan adanya selisih yang terjadi antara proses las TBW dan proses las pengaruh PWHT cukup besar maka bisa dikatakan bahwa pengelasan TBW belum bisa mnggantikan proses PWHT. ABSTRACT Welding technology in the pressure vessel fabricating process is rapidly developed nowadays, which is needed to obatain the qualified result of the weldments, so that the special treatment for the pressure vessel such as post weld heat treatment(PWHT) must applied. PWHT process must be done especially in the oil and gas, petrochemical, power plant projects, etc. Based on the Welding Technology of Australia (WTIA), one of the applicable method to substitute the PWHT process is a method called Temper Bead Welding (TBW). In this final project, results of PWHT process will be compared to the results of TBW, both alternate temperbead technique and weld toe tempering technique. Material used in this project is SA 516 grade 70 with GMAW process. PWHT process itself will be done in a furnace with 595 o C holding temperature, and the holding time applied is 1 hour. Welding technique from both methods will compared through some tests such like hardness test, impact test, and metallography test to make sure how exactly is the fluence of TBW method can substitute the PWHT process. Results that obtained from this final project is , microstructure in the HAZ become fine grain – shape. It’s relates to the hardness value that tend to be more ductile caused by tempering process that occured in the HAZ. With average hardness value at the PWHT is 170,12 HVN, 212,47 HVN at the alternate temper bead technique, 221,21 HVN at the weld toe tempering technique. Hardness value in the temperbead welding is much more higher than the PWHT process . Whereas impact testing at a temperature of -15 o C shows the greater differential between PWHT process is 1,5 J/mm 2 , and TBW – weld toe tempering technique 0,94 J/mm 2 , so that the impact value differential between PWHT process and TBW process is 0,56 J/mm 2 . From those differential values between PWHT process and TBW process, we may conclude that TBW methods not yet applicable to substitute the PWHT process. Keywords: temper bead welding, PWHT, hardness test, impact test, and

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 24 Aug 2018 06:33
Last Modified: 24 Aug 2018 06:33
URI: http://repository.ppns.ac.id/id/eprint/68

Actions (login required)

View Item View Item