Syaelendra, Endric (2016) STUDI PEMANFAATAN LIMBAH SANDBLASTING PADA PT. X SEBAGAI BAHAN CAMPURAN BETON RINGAN. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.
Full text not available from this repository.Abstract
ABSTRAK Limbah sandblasting merupakan salah satu jenis limbah B3 berdasarkan PP No. 101 Tahun 2014 dengan bahaya kategori 2. Limbah sandblasting mengandung logam berat maka perlu dilakukan penanganan khusus sebelum dibuang ke lingkungan. Selain logam berat, limbah sandblasting juga mengandung silika dioksida (SiO2) yang tinggi sehingga dapat dimanfaatkan sebagai campuran bahan bangunan. Pemanfaatan limbah sandblasting sebagai beton ringan dapat dijadikan sebagai solusi dalam upaya pencegahan pencemaran limbah B3. Penelitian ini bertujuan untuk menganalisa penambahan limbah sandblasting terhadap waktu pengikatan semen, kuat tekan, berat jenis dan tingkat keamanan penggunaan limbah sandblasting berdasarkan hasil uji TCLP. Penelitian ini menggunakan benda uji berbentuk silinder dengan dimensi Ø 15 cm dan tinggi 30 cm. Komposisi campuran limbah sandblasting sebagai substitusi semen sebesar 0% ; 10% ; 15% ; 20% dan 25% dengan FAS sebesar 0,3 dan agregat kasar berupa batu apung. Hasil penelitian pada beton ringan umur 28 hari menunjukkan bahwa limbah sandblasting dengan komposisi 10% dan 15% mengalami kenaikan kuat tekan sebesar 6,23% dan 6,99% sedangkan pada komposisi 20% dan 25% mengalami penurunan kuat tekan sebesar 12,93% dan 9,96% dari beton ringan normal (0%) sebesar 10,44 Mpa. Berat jenis yang dihasilkan pada komposisi 0% ; 10% ; 15% ; 20% ; dan 25% secara berturut – turut sebesar 1640,25 kg/m 3 ; 1672,96 kg/m 3 ; 1642,77 kg/m 3 ; 1667,92 kg/m 3 ; dan 1709,43 kg/m 3 . Hasil pengujian setting time dengan komposisi 10% ; 15% ; 20% ; dan 25% menghasilkan waktu pengikatan awal semen secara berturut – turut sebesar 83,07 menit ; 97,5 menit ; 98,75 menit ; dan 109,09 menit dan waktu pengikatan akhir semen sebesar 165 menit ; 180 menit ; 180 menit ; dan 195 menit lebih lama dibandingkan dengan waktu ikat awal dan akhir semen tanpa campuran limbah sandblasting sebesar 80,77 menit dan 150 menit. Hasil uji TCLP limbah sandblasting sebelum dan sesudah disolidifikasi dengan kandungan logam berat Cu, Cr 6+ , Cd, Hg, Pb, Ni dan Zn telah memenuhi baku mutu yang ditetapkan oleh PP No. 101 Tahun 2014 dengan penurunan kandungan logam berat setelah disolidifikasi secara berturut – turut sebesar 53,53% ; 51,22% ; 54,94% ; 70,97% ; 30,77% ; 42,93% ; dan 20,25%. Kata kunci : Limbah Sandblasting, Beton Ringan, Setting Time, Berat Jenis, Kuat Tekan, Uji TCLP. ABSTRACT Sandblasting waste is one types of hazardous waste under PP No. 101 Year 2014 with the hazard category 2. Sandblasting waste containing heavy metals which is necessary to do special treatment before being discharged into the environment. In addition to heavy metal, sandblasting waste also contains high silica dioxide (SiO 2) so that can be used as a building material mixture. Sandblasting waste utilization as lightweight concrete can be used as a solution in prevention of pollution of hazardous waste. This study aims to analyze the addition of sandblasting waste to the setting time of cement, compressive strength, density and level of safety of use sandblasting waste based on TCLP test results. This study uses a cylindrical specimen with dimensions Ø 15 cm and 30 cm high. Sandblasting waste mixture composition as a cement substitute is 0% ; 10% ; 15% ; 20% ; and 25% with FAS at 0,3 and coarse aggr egate is pumice. The results of research on lightweight concrete with aged 28 days showed that sandblasting waste with the composition of 10% and 15% can improve the compressive strength by 6,23% and 6,99% while the composition of 20% and 25% of the compressive strength decreased by 12,93% and 9,96% from the normal lightweight concrete (0%) amounted to 10,44 MPa. Density generated on the composition of 0%, 10%, 15%, 20% and 25% respectively is 1640,25 kg/m 3 ; 1672,96 kg/m 3 ; 1642,77 kg/m 3 ; 1667,92 kg/m 3 ; and 1709,43 kg/m 3 . The result of setting time test with the composition by 10% ; 15% ; 20% ; and 25% produced an initial setting time of cement respectively by 83,07 minutes ; 97,5 minutes ; 98,75 minutes ; and 109,09 minutes and final setting time of cement respectively by 165 minutes ; 180 minutes ; 180 minutes ; and 195 minutes more longer than initial setting time and final setting time cement without sandblasting waste mixture respectively by 80,77 minutes and 150 minutes. The result of TCLP test of sandblasting waste before and after solidification with the contents of heavy metal Cu, Cr 6+ , Cd, Hg, Pb, Ni and Zn have value below the quality standard of PP 101 Year 2014 with a reduction in heavy metal contents after solidification respectively by 53,53% ; 51,22% ; 54,94% ; 70,97% ; 30,77% ; 42,93% ; and 20,25%. Keyword: Sandblasting Waste, Lightweight Concrete, Setting Time, Density, Compressive Strength, TCLP Test.
| Item Type: | Thesis (Diploma) |
|---|---|
| Subjects: | T Technology > T Technology (General) |
| Divisions: | ?? tkdkk ?? |
| Depositing User: | Unnamed user with email repository@ppns.ac.id |
| Date Deposited: | 13 Sep 2018 04:40 |
| Last Modified: | 13 Sep 2018 04:40 |
| URI: | http://repository.ppns.ac.id/id/eprint/626 |
Actions (login required)
 |
View Item |