ANALISA PENGARUH PARAMETER PENGELASAN SPOT WELDING TERHADAP SHEAR STRENGTH DENGAN METODE TAGUCHI PADA SUS 304

Fabyola, Sugiarto (2014) ANALISA PENGARUH PARAMETER PENGELASAN SPOT WELDING TERHADAP SHEAR STRENGTH DENGAN METODE TAGUCHI PADA SUS 304. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Pada proses pengelasan spot welding tidak dapat dihindari bahwa mutu dari proses pengelasan ini sangat diperhatikan. Mutu las tersebut harus memiliki persyaratan yang baik ditinjau dari bahan – bahan yang digunakan dan parameter -parameter proses pengelasan spot welding seperti: welding current, welding time dan force. Untuk mengoptimalkan kualitas produk dan proses dalam waktu yang bersamaan maka diperlukan suatu metode optimasi. Pada penelitian ini, dilakukan proses pengelasan menggunakan mesin spot welding dengan kombinasi parameter sesuai dengan desain eksperimen yang telah dirancang dan melakukan pengujian tarik pada tiap-tiap kombinasi parameter, dimana hasil input yang berupa kekuatan tarik tersebut kemudian diolah dengan menggunakan metode Taguchi. Selanjutnya, setelah didapatkan kombinasi yang paling optimum, dilakukan perhitungan persentase kontribusi untuk mengetahui seberapa besar masing – masing parameter memberikan kontribusi pada pengelasan spot welding. Hasil yang didapat setelah dilakukan pengolahan data yaitu, nilai shear strength yang terjadi untuk setiap welding current, welding time dan force pada pengelasan spot welding yang berbeda adalah range 1500 kgf sampai dengan 2000 kgf. Dimana telah didapat kombinasi parameter yang optimum yaitu, welding current 9,5 kA, welding time 0,5 sekon dan force 800 kgf. Diantara ketiga faktor, welding current yang memberikan kontribusi yang paling besar yaitu 43,51 %, lalu force dengan kontribusi 9,59 % dan yang terakhir adalah welding time dengan kontribusi 7,04 %. Kata kunci : Spot Welding, Metode Taguchi, Parameter Pengelasan Spot Welding ABSTRACT On spot welding process, it is inevitable that the quality of the process are concerned. The weld quality should have a good requirements in terms of materials used and spot welding process parameters such as welding current, welding time and force. To optimize the quality of products and processes at the same time, it would require a method of optimization. On this research, carried process with combination of spot welding machine parameters according to experiment design that has been designed and tested pull on each parameter combination, which results in the form of tensile strength input then processed using Taguchi method. Furthermore, after the most optimum combination is obtained, the percentage contribution be calculated to find out how much each -parameter contributes on spot welding. The results after data processing is carried, value of shear strength that occurs for each welding current, welding time and force on different spot welding are range of 1500 kgf to 2000 kgf. Where have obtained the optimum combination of parameters, namely, 9.5 kA welding current, welding time of 0.5 second and a force of 800 kgf. Among three factors, welding current which gives the greatest contribution is 43.51%, and 9.59% contribution to the force and the latter is the welding time by contributing 7.04%. Keywords: Spot Welding, Taguchi Methods, Spot Welding Parameters

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > D3 Teknik Bangunan Kapal
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 24 Aug 2018 04:12
Last Modified: 24 Aug 2018 04:12
URI: http://repository.ppns.ac.id/id/eprint/57

Actions (login required)

View Item View Item