Studi Pengaruh Bending Terhadap Thickness Coat 3-Layer Polyethylene pada Letang, Tengah, dan Rawa Optimazion Pipeline Project

Farabi, Daya Alam (2015) Studi Pengaruh Bending Terhadap Thickness Coat 3-Layer Polyethylene pada Letang, Tengah, dan Rawa Optimazion Pipeline Project. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Pada pipa 12” menggunakan coat 3-Layer Polyethylene yang digunakan untuk mendistribusikan gas dari stasiun Rawa ke Grissik Central Gas yang berjarak 51.25 km. terdapat lekukkan tanah yang mengharuskan pipa untuk dibending pada derajat dan radius tertentu. Setalah dibending pipa tersebut diinspeksi menggunakan Ultrasonic Test. Untuk mencegah terjadinya crack pada setiap lapisan coating dan pipanya. Namun penggunaan inspeksi Ultrasonic Test terlalu memakan waktu dan biaya bagi pihak konstruksi. Dari permasalahan di atas dilakukan analisa dengan membandingkan nilai thickness pipa dan coat sebelum dan sesudah dibending menggunakan perhitungan manual field bend dan inspeksi Ultrasonic Test. sehingga bisa diketahui nilai penurunan thickness pipa dan coat nya, serta mengetahui nilai bending stress sebelum dan sesudah proses bending. Dari Penelitian didapatkan untuk nilai wall thickness sebesar 12,8 mm dan masih diijinkan untuk digunakan karena D/t nilainya masih lebih kecil dari 96. Untuk perhitungan field bend menggunakan manual nilai (wall thickness pipa, Coating thickness, dan penjumlahan keduannya) mengalami penurunan thickness paling besar pada radius 25D menjadi 11,25 mm, 2.56 mm dan 13,81 mm. menggunakan inspeksi menjadi 10,76 mm, 2,55 mm, dan 13,31 mm. Untuk perhitungan manual bending stress sebelum proses bending didapatkan nilai sebesar 33,5 MPa, sedangkan nilai bending stress setelah proses bending menggunakan software Intergraph Caesar II pada derajat bending 0,74° hingga 2,68° didapatkan sebesar 122,87 MPa hingga 440 MPa. Nilai bending stress pada derajat bending 0,74° hingga 1,67° masih diijinkan dikarenakan nilainya masih kurang dari nilai allowable stress yaitu 324 MPa. Namun nilai bending stress pada derajat bending 2,23° dan 2,68° tidak diijinkan karena nilainya di atas nilai allowable stress yaitu 324 MPa. Kata Kunci : Bending, Pipeline, Field Bend, Coating, 3-Layer Polyethylene. ABSTRACT On pipe 12" using 3-Layer Polyethylene coat used to distribute gas from the station to Grissik Central Swamp Gas within 51.25 km. There are lands that require bend pipe to bend on degree and a certain radius. After that, pipe bend inspected using Ultrasonic test. To prevent the occurrence of crack on each layer of coating and pipe. However, the use of inspection Ultrasonic Test too takes a lot of time and costs for the construction.. From the analysis above problems by comparing the manual calculation field bend and inspection using Ultrasonic Test. so they can know the value of a decrease in thickness of pipe and coat, and knows the value of bending stress before and after the bending process. Trial obtained the value of wall thickness are used, manual Field bend calculation comparison with the results of the inspection, and the bending stress values before and after dibending. Value obtained 12.8 mm wall thickness and still be allowed to be used as D / t value is still smaller than 96. To use the manual calculation of bend field values (the pipe wall thickness, coating thickness, and both) experienced the greatest decrease in thickness at 25D radius to 11.25 mm, 2.56 mm and 13.81mm. inspection be 10.76 mm, 2.55 mm, and 13.31 mm. For manual calculation of bending stress before bending process obtained a value of 33.5 MPa,. bending stress value after the bending process using Intergraph Caesar II software on the degree of bending of 0.74 ° to 2.68 ° obtained by 122.87 MPa to 440 MPa. Value bending stress on the degree of bending of 0.74 ° to 1.67 ° is permissible because the value is still less than the allowable stress is 324 MPa. However, the value of bending stress on the degree of bending of 2.23 ° and 2.68 ° is not allowed because they are above the allowable stress values is 324 MPa. Keyword : Bending, Pipeline, Field Bend, Coating, 3-Layer Polyethylene.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Permesinan Kapal > Teknik Perpipaan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 10 Sep 2018 05:25
Last Modified: 10 Sep 2018 05:25
URI: http://repository.ppns.ac.id/id/eprint/499

Actions (login required)

View Item View Item