ANALISA PROTEKSI KATODIK MENGGUNAKAN SISTEM ICCP (IMPRESSED CURRENT CATHODIC PROTECTION) PADA PIPA BAWAH TANAH

PRASETYA B., RAHMAT HIDAYAT (2015) ANALISA PROTEKSI KATODIK MENGGUNAKAN SISTEM ICCP (IMPRESSED CURRENT CATHODIC PROTECTION) PADA PIPA BAWAH TANAH. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Korosi adalah kerusakan material pada logam akibat reaksi dengan lingkungan. Korosi merupakan salah satu permasalahan yang sering terjadi pada industri yang menggunakan peralatan bahan material logam. Korosi tidak dapat dihilangkan akan tetapi dapat dicegah. Salah satu cara pencegahan korosi pada pipa dapat dilakukan dengan cara menggunakan coating dan menerapkan sistem proteksi katodik., dalam hal ini sistem yang dipakai adalah sistem Impressed Current Cathodic Protection (ICCP). Pada tugas akhir ini, dilakukan pengujian menggunakan variasi pH dan variasi anoda. Material yang digunakan dalam pengujian menggunakan API 5L grade B, kemudian melakukan pengujian untuk mengetahui laju korosi antara anoda Grafite, Cu dan Mg. Pengujian dilakukan selama 5 hari pada anoda Grafite, Cu dan Mg dengan nilai pH tanah yang berbeda, kemudian untuk mengetahui nilai laju korosi dapat diperoleh menggunakan metode kehilangan berat. Hasil pengujian menunjukan bahwa nilai pH dapat mempengaruhi nilai laju korosi. Semakin rendah nilai pH tanah maka semakin besar tingkat laju korosi yang terjadi dan apabila semakin tinggi nilai pH tanah maka semakin kecil tingkat laju korosi yang terjadi. Dari perbandingan nilai laju korosi pada anoda Grafite, Cu dan Mg yang tahan terhadap korosi adalah anoda Grafite dengan nilai laju korosi pada pH 5 sebesar 0,043 mpy, nilai laju korosi pada pH 6 sebesar 0,027 mpy, dan nilai laju korosi pada pH 7 sebesar 0,016 mpy. Dari perhitungan umur anoda yang paling lama terjadi pada anoda grafite dengan nilai life time 11,3 tahun, kemudian nilai life time anoda Cu sebesar 10,9 tahun dan nilai life time anoda Mg sebesar 10,6 tahun. Kata Kunci : Korosi, Impressed Current Cathodic Protection, Anoda, laju korosi, API 5L Grade B ABSTRACT . Corrosion is material damage to the metal due to reaction environment. Corrosion is one of the problems that often occur in industries that use equipment metallic materials. Corrosion can not be eliminated but can be prevented. One way of preventing corrosion of pipes can be done by using the coating and applying cathodic protection system, in this case the system is the system used Impressed Current Cathodic Protection (ICCP). In this final project, test is carried using a pH variation and variation anode. Materials used in the test using the API 5L grade B, then do a test to compare the corrosion rate between the anode Grafite, Cu and Mg. Tests conducted 5 days at the anode Grafite, Cu and Mg with different soil pH value, then to determine the value of corrosion rate can be obtained using methods weight loss. Test results showed that the pH value can affect the value of corrosion rate. From the comparison of the rate of corrosion at the anode Grafite, Cu and Mg are resistant to corrosion is anode Grafite with the greatest rate of 0.043 mpy on soil pH 5 and the smallest corrosion rate of 0.016 mpy on soil pH 7. Anode Cu with the greatest rate of 1,287 mpy on soil pH 5 and the smallest corrosion rate of 0,831 mpy on soil pH 7, while for anodes that are susceptible to corrosion is anode Mg with the largest value of 6.890 mpy corrosion rate at pH 5 and the smallest corrosion rate of 3.922 mpy on soil pH 7. In the life time calculation of the oldest anode is the anode Grafite is 11.3 years, and then the anode Cu is 10.9 years and the anode Mg is 10.6 years Keyword : Corrosion, Impressed Current Cathodic Protection, Anode, Corrosion Rate, API 5L Grade B

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Permesinan Kapal > Teknik Perpipaan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 10 Sep 2018 03:47
Last Modified: 10 Sep 2018 03:47
URI: http://repository.ppns.ac.id/id/eprint/477

Actions (login required)

View Item View Item