ANALISIS PENGARUH IN SERVICE REPAIR TERHADAP KEKERASAN DAN STRUKTUR MIKRO”.

Imanu, Shinjikko Dhamar (2015) ANALISIS PENGARUH IN SERVICE REPAIR TERHADAP KEKERASAN DAN STRUKTUR MIKRO”. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Dalam industri dan proyek pembangunan, pipeline merupakan suatu bagian yang vital dan dikerjakan secara berhati-hati. Pengerjaan pipeline ini harus dikerjakan sesuai dengan standar yang berlaku. Karena menurut fungsi penggunaannya pipeline sendiri digunakan untuk beberapa aplikasi, seperti pipa untuk transportasi gas maupun liquid. Oleh karena itu pengerjaan dari sistem pipeline ini harus benar benar diperhatikan selama porses pengerjaannya dan cacat pennglasan pada pipelines bisa terjadi dan untuk menghemat waktu dilakukan ialah repair pada pipa mengalami cacat. pipeline. Pipa yang mengalami cacat ialah pipa jalur pipeline yang mengalirkan liquid. Namun untuk merepairnya dilakukan dengan tetap mengalirkan fluida yang ada didalam pipa tersebut Hal tersebut mengakibatkan struktur mikro pada pipa tersebut berubah. Karena terjadi perubahan struktur mikro maka sifat mekaniknya juga berubah. Maka dilakukan pengelasan degan mengaliri air dan udara bertekanan pada pipa dan pengelasan tanpa mengaliri fluida pada pipa sebagai pembanding untuk mengetahui kuat tarik, kekerasan dan struktur mikro. Pengujian kekerasan nilai kekerasan paling tinggi adalah pada spesimen pengelasan di aliri fluida air, memiliki nilai kekerasan rata-rata yaitu base metal A160, 57HVN, HAZ A143,77, HVN weld metal 168,3HVN, HAZ b134,59 HVN, base metal b146,87. nilai kekerasan terbesar yang ke-2 terdapat pada pada spesimen pengelasan di aliri fluida udara bertekanan memiliki nilai kekerasan rata-rata yaitu base metal A 130,27 HVN, HAZ A 145,96 HVN weld metal 162,96 HVN, HAZ b 133,54 HVN, base metal b 147,61 HVN. Dan nilai kekerasan terendah terdapat pada spesimen pengelasan tanpa aliran fluida memiliki nilai rata-rata yaitu base metal a 129,45 HVN, HAZ a 148,07 HVN dan weld metal 164,76 HVN, HAZ b 131,24 HVN, base metal b 149,17 HVN Pada pengujian struktur mikro spesimen pengelasan dengan fluida air struktur pearlite lebih banyak terbentuk dari pada spesimen pengelasan dengan fluida udara bertekanan dan tanpa fluida Kata Kunci : fluida, kekerasan, struktur mikro. ABSTRACT In industry and development projects, the pipeline is a vital part and is done carefully. The work of this pipeline must be done in accordance with applicable standards. Because according to the use of its own pipeline function is used for some applications, such as pipelines for gas and liquid transportation. Therefore, the work of this pipeline system must be properly observed during the processing portion and defects in pipe lines can occur and to save time is repaired on the defective pipe. pipeline. The defective pipes are pipeline pipes that drain the liquid. However, for merepairnya is done by still flowing fluid i n the pipe It causes the micro structure in the pipe is changed. Because of changes in microstructure, the mechanical properties also change. Then welding degan flowing water and air pressurized on the pipe and welding without flowing fluid in the pipe as a comparison to know the tensile strength, hardness and micro structure. The highest hardness hardness testing is on the welding specimens in water fluid aliases, has a mean hardness value of base metal A160, 57HVN, HAZ A143,77, HVN weld metal 168,3HVN, HAZ b134,59 HVN, base metal b146, 87. the 2nd largest hardness value is found in the welded specimens in the aliquots of the pressurized air fluid having a mean hardness value of A metal base A 130.27 HVN, HAZ A 145.96 HVN weld metal 162.96 HVN, HAZ b 133.54 HVN, base metal b 147,61 HVN. And the lowest hardness values found in the welding specimens without fluid flow have a mean value of base metal a 129.45 HVN, HAZ 148.07 HVN and 164.76 HVN weld metal, HAZ b 131.24 HVN, base metal b 149 , 17 HVN In microstructure testing of welded specimens with water fluid pearlite structures are more formed than welded specimens with pressurized and non-fluid air fluid Keywords: fluid, hardness, micro structure.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 07 Sep 2018 05:54
Last Modified: 07 Sep 2018 05:54
URI: http://repository.ppns.ac.id/id/eprint/386

Actions (login required)

View Item View Item