PENGARUH VARIASI KUAT ARUS DAN FILLER METAL PADA PENGELASAN PIPA CARBON FE 330 DENGAN SA 106 Gr.B TERHADAP MECHANICAL PROPERTIES, STRUKTUR MIKRO SERTA CORROSION RATE

SA’DAN, AHMAD (2015) PENGARUH VARIASI KUAT ARUS DAN FILLER METAL PADA PENGELASAN PIPA CARBON FE 330 DENGAN SA 106 Gr.B TERHADAP MECHANICAL PROPERTIES, STRUKTUR MIKRO SERTA CORROSION RATE. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Dalam proses pembangunan suatu pabrik dimana terdapat proses fabrikasi dan juga proses pengelasan yang digunakan sebagai metode penyambungannya, maka pemilihan proses pengelasan harus disesuaikan dengan material yang akan disambung. Pemilihan material sendiri disesuaikan dengan kegunaannya dan tujuan pemakaian. Salah satunya yaitu material pipa carbon steel . Pipa carbon steel juga terdapat berbagai macam jenis, diantaranya yaitu material pipa FE330 dan SA 106 Gr.B. Material SA 106 Gr.B mempunyai kandungan karbon lebih banyak dibanding material FE330, namun kondisi aktual di lapangan, line pipa FE330 disambung dengan pipa SA 106 Gr B karena kehabisan stok pipa FE330, Hal tersebut disebabkan karena pipa FE330 sangatlah jarang dijual dipasaran dan harus inden terlebih dahulu untuk pemesanannya. Pada penelitian ini pipa karbon FE330 disambung dengan pipa SA 106 Gr.B dengan variasi kuat arus pengelasan sebesar 80 A, 100 A, dan 120 A dan dengan variasi filler metal ER 70S-6 dan ER 70S-G. Berdasarkan hasil penelitian didapatkan bahwa pengelasan dengan filler metal ER 70S-6 dan kuat arus 80 A lebih bagus jika dibandingkan dengan variasi lainnya, yang mana dapat dibuktikan dengan hasil uji tarik, uji bending, nilai hardness , struktur mikro, serta uji korosi. Kata-kata kunci : Carbon steel, SA 106 Gr.B, FE330, kuat arus, filler metal ER 70S-6 dan ER 70S-G. ABSTRACT In the process of development of a plant where there is a process of fabrication and welding processes are also used as a method of these connections, then the selection of the welding process must be adapted to the material to be spliced. Selection of the material itself adapted to the usefulness and purpose of use. One of which is carbon steel pipe material. Carbon steel pipe also there are various kinds, among which the pipe material FE330 and SA 106 Gr.B. SA 106 Gr.B material has a carbon content of more than FE330 material, but the actual conditions in the field, line pipes FE330 connected with pipes SA 106 Gr B due to out of stock pipes FE330, This is because the pipes FE330 is rarely sold in the market and must pivot prior to ordering. In this study, FE330 carbon pipe connected to the pipe SA 106 Gr.B with strong variation of the welding current is 80 A, 100 A, and 120 A and with a variety of filler metal ER 6 and ER 70S-70S-G. Based on the results of the research showed that the welding with filler metal ER 70S-6 and strong currents of 80 A better if compared with other variations, which can be proved by the results of tensile test, bending test, hardness value, microstructure, and corrosion test Key words : Carbon steel, SA 106 Gr.B, FE330, current, filler metal ER 70S-6 and ER 70S-G.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 07 Sep 2018 05:26
Last Modified: 07 Sep 2018 05:26
URI: http://repository.ppns.ac.id/id/eprint/378

Actions (login required)

View Item View Item